Flame Retardancy of Whisker Silicon Oxide/Rigid Polyurethane Foam Composites with Expandable Graphite

被引:36
作者
Bian, Xiang-Cheng [1 ,2 ,3 ]
Tang, Jian-Hua [1 ]
Li, Zhong-Ming [2 ]
机构
[1] Sichuan Univ, Coll Chem Engn, Chengdu 610065, Peoples R China
[2] Sichuan Univ, State Key Lab Polymer Mat Engn, Coll Polymer Sci & Engn, Chengdu 610065, Peoples R China
[3] Sichuan Univ, Coll Chem, Ctr Degradable & Flame Retardant Polymer Mat, Chengdu 610064, Peoples R China
基金
中国国家自然科学基金;
关键词
polyurethane foams; expandable graphite; whisker silicon; flame retardant properties; mechanical properties;
D O I
10.1002/app.28921
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Rigid polyurethane foam (RPUF) composites filled with various expandable graphite (EG) or/and whisker silicon (WSi) loadings were prepared with the same density (0.08 g/cm(3)). When the WSi content reached 10 wt %, the composite had the best mechanical properties, the values of compressive strength and modulus reached 0.74 and 21.0 MPa, respectively. Compared with only EG filled RPUF, the addition of 10 wt % WSi to EG/RPUF would also bring out improvement on their flame retardant and mechanical properties. Maintaining EG 20 wt %,, the compressive strength increased from 0.17 (EG/RPUF) to 0.39 MPa (WSi/EG/RPUF), the compressive modulus increased from 9.32 (EG/RPUF) to 10.1.1 MPa (WSi/EG/RPUF), and the limiting oxygen index value increased from 28 vol % (EG/RPUF) to 32.5 vol % (WSi/EG/RPUF). The thermogravimetric analysis showed that the addition of EG and WSi particles improved the thermal stabitity of the composites. The dynamical mechanical analysis (DMA) showed that EG and WSi particles led to up-shift of the glass transition temperature. Moreover, 10 wt 9% EG and 10 wt % WSi filled RPUF had the highest storage modulus, as the EG and WSi exhibited a desirable synergetic effect on flame retardant properties and dynamic mechanical properties of RPUF composites. The morphologies of the composites were analyzed with scanning electron microscopy. (C) 2008 Wiley Periodicals, Inc. J Appl Polym Sci 110: 3871-3879, 2008
引用
收藏
页码:3871 / 3879
页数:9
相关论文
共 50 条
  • [41] Expandable graphite for halogen-free flame-retardant of high-density rigid polyurethane foams
    Shi, L
    Li, ZM
    Yang, MB
    Yin, B
    Zhou, QM
    Tian, CR
    Wang, JH
    [J]. POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING, 2005, 44 (07) : 1323 - 1337
  • [42] Flame retardancy of different-sized expandable graphite particles for high-density rigid polyurethane foams
    Shi, Lei
    Li, Zhong-Ming
    Xie, Bang-Hu
    Wang, Jian-Hua
    Tian, Chun-Rong
    Yang, Ming-Bo
    [J]. POLYMER INTERNATIONAL, 2006, 55 (08) : 862 - 871
  • [43] FTIR spectroscopic measurement of halogenated compounds produced during fire suppression tests of two halon replacements
    Su, JZ
    Kim, AK
    Kanabus-Kaminska, M
    [J]. FIRE SAFETY JOURNAL, 1998, 31 (01) : 1 - 17
  • [44] Taesler C, 1996, J APPL POLYM SCI, V61, P783, DOI 10.1002/(SICI)1097-4628(19960801)61:5<783::AID-APP9>3.0.CO
  • [45] 2-K
  • [46] Effect of natural fibers on thermal and mechanical properties of natural fiber polypropylene composites studied by dynamic mechanical analysis
    Tajvidi, Mehdi
    Falk, Robert H.
    Hermanson, John C.
    [J]. JOURNAL OF APPLIED POLYMER SCIENCE, 2006, 101 (06) : 4341 - 4349
  • [47] Flexural properties of mica filled polyurethane foams
    Vaidya, NY
    Khakhar, DV
    [J]. JOURNAL OF CELLULAR PLASTICS, 1997, 33 (06) : 587 - &
  • [48] Physical and chemical effects of diethyl N,N′-diethanolaminomethylphosphate on flame retardancy of rigid polyurethane foam
    Wang, XL
    Yang, KK
    Wang, YZ
    [J]. JOURNAL OF APPLIED POLYMER SCIENCE, 2001, 82 (02) : 276 - 282
  • [49] Morphology and mechanical properties of nylon-1010-filled rigid polyurethane foams
    Yin, B
    Li, ZM
    Quan, H
    Yang, MB
    [J]. JOURNAL OF ELASTOMERS AND PLASTICS, 2004, 36 (04) : 333 - 349
  • [50] ZHONG ZY, 2004, POLYM INT, V53, P1093