(Y2O3-GeO2) phosphor thin-film electroluminescent emitting layers prepared by magnetron sputtering

In this paper, new multicomponent oxides are shown to be promising as a host material for the phosphor thin-film emitting layer of thin-film electroluminescent (TFEL) devices. Mn-activated (Y2O3-GeO2) multicomponent oxide phosphor thin films were prepared by r.f. magnetron sputtering and used as the emitting layer of TFEL devices. High luminance multicolor emissions were obtained in TFEL devices using (Y2O3-GeO2):Mn thin films prepared with a GeO2 content of 0-100 mol.%. In a yellow emitting TFEL device fabricated using a Y2GeO5 phosphor thin film prepared with a GeO2 content of approximately 50 mol.%, a high luminance of 758 cd/m(2) and a luminous efficiency of 1.4lm/W were obtained when driven by a sinusoidal wave voltage at 1 kHz. (C) 2001 Elsevier Science B.V. All rights reserved.