The role of stress-state on the deformation and fracture mechanism of hydrided and non-hydrided Zircaloy-4

被引:14
作者
Cockeram, B. V. [1 ]
Hollenbeck, J. L. [1 ]
机构
[1] Bechtel Marine Prop Corp, Bettis Lab, West Mifflin, PA 15122 USA
关键词
Zircaloy; Mechanical properties; Stress state; Fracture; DUCTILE FRACTURE; IN-SITU; PRECIPITATE STABILITY; TOUGHNESS MEASUREMENT; ZIRCONIUM ALLOYS; PRESSURE; GROWTH; BEHAVIOR; RUPTURE; MODEL;
D O I
10.1016/j.jnucmat.2015.09.012
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Zircaloy-4 was tested at room-temperature over a range of hydrogen content between 10 and 200 ppm, and stress-states between a triaxiality of -0.23 and 0.9. Triaxiality (eta) is defined as the ratio of hydrostatic stress to von Mises stress and was controlled through use of select mechanical test specimen designs. Testing of smooth and notched tensile specimens (eta = 0.33 to 0.9) results in an increase in the stress to initiate plastic deformation and a decrease in strain to failure at higher values of eta. Increases in triaxiality are shown to have a more significant effect on reducing the strain to failure when the material is hydrided. Increases in strain to failure are observed at lower values of triaxiality for dual keyhole specimens (eta = 0.1) and compression specimens (eta = -0.17 to -0.23), with hydrided material showing much less decrement in strain to failure at these lower triaxialities. Examinations of microstructure are used to show that a change in mechanism for deformation and fracture with triaxiality can explain these differences in mechanical behavior and a model is developed to describe the observed changes in strain to failure with stress-state. (C) 2015 Elsevier B.V. All rights reserved.
引用
收藏
页码:9 / 31
页数:23
相关论文
共 73 条
[1]  
Adamson R, 2013, MECH TESTING ZIRCONI, VI
[2]  
[Anonymous], 2013, E813A ASTM INT
[3]   FINITE-ELEMENT ANALYSIS OF VOID GROWTH NEAR A BLUNTING CRACK TIP [J].
ARAVAS, N ;
MCMEEKING, RM .
JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1985, 33 (01) :25-49
[4]   COMPOSITION OF PRECIPITATES PRESENT IN ZIRCALOY-2 AND ZIRCALOY-4 [J].
ARIAS, D ;
PALACIOS, T ;
TURRILLO, C .
JOURNAL OF NUCLEAR MATERIALS, 1987, 148 (02) :227-229
[5]   HYDRIDE EMBRITTLEMENT IN ZIRCALOY-4 PLATE .1. INFLUENCE OF MICROSTRUCTURE ON THE HYDRIDE EMBRITTLEMENT IN ZIRCALOY-4 AT 20-DEGREES-C AND 350-DEGREES-C [J].
BAI, JB ;
PRIOUL, C ;
FRANCOIS, D .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1994, 25 (06) :1185-1197
[6]   A new model of metal plasticity and fracture with pressure and Lode dependence [J].
Bai, Yuanli ;
Wierzbicki, Tomasz .
INTERNATIONAL JOURNAL OF PLASTICITY, 2008, 24 (06) :1071-1096
[7]   In situ crack growth observation and fracture toughness measurement of hydrogen charged Zircaloy-4 [J].
Bertolino, G ;
Meyer, G ;
Ipiña, JP .
JOURNAL OF NUCLEAR MATERIALS, 2003, 322 (01) :57-65
[8]   Ductile-to-brittle transition temperature for high-burnup cladding alloys exposed to simulated drying-storage conditions [J].
Billone, M. C. ;
Burtseva, T. A. ;
Einziger, R. E. .
JOURNAL OF NUCLEAR MATERIALS, 2013, 433 (1-3) :431-448
[9]  
Bridgman PW., 1952, STUDIES LARGE PLASTI
[10]   A FRACTURE MODEL FOR HYDRIDE-INDUCED EMBRITTLEMENT [J].
CHAN, KS .
ACTA METALLURGICA ET MATERIALIA, 1995, 43 (12) :4325-4335