Step-freeze-drying method for carbon aerogels: a study of the effects on microstructure and mechanical property

被引：40

作者：

Hu, Lei ^{[1
,2
]}

He, Rujie ^{[1
,2
]}

Lu, Zhang ^{[1
,2
]}

Zhang, Keqiang ^{[1
,2
]}

Bai, Xuejian ^{[1
,2
]}

机构：

[1] Beijing Inst Technol, Inst Adv Struct Technol, Beijing 100081, Peoples R China

[2] Beijing Inst Technol, Beijing Key Lab Lightweight Multifunct Composite, Beijing 100081, Peoples R China

来源：

RSC ADVANCES | 2019年 / 9卷 / 18期

基金：

中国国家自然科学基金; 北京市自然科学基金;

关键词：

THERMAL-CONDUCTIVITY; RESORCINOL; POLYCONDENSATION; MESOPOROSITY; ELECTRODES; GELS;

D O I：

10.1039/c9ra01328h

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

In this paper, a novel step-freeze-drying method was used to prepare carbon aerogels. The effects of step-freeze-drying on the density, linear shrinkage, specific surface area, pore size distribution, microstructure and compressive strength of carbon aerogels were investigated, and compared to traditional freeze-drying methods. It was found that the step-freeze-drying method reduced the density, linear shrinkage and pore size of carbon aerogels compared to traditional freeze-drying. And it also improved the specific surface area, the microstructural homogenization and the compressive strength of carbon aerogels compared to traditional freeze-drying. It is therefore believed that step-freeze-drying is an efficient method to obtain carbon aerogels with fine microstructure and high mechanical property.

引用

页码：9931 / 9936

页数：6

共 27 条

[1]

Aegerter M. A., 2011, AEROGELS HDB, DOI DOI 10.1007/978-1-4419-7589-8_4

[2]

Al-Muhtaseb S. A., 2010, ADV MATER, V15, P101, DOI DOI 10.1002/adma.200390020

[3] Novolac-derived carbon aerogels pyrolyzed at high temperatures: experimental and theoretical studies [J].

Allahbakhsh, Ahmad ;

Bahramian, Ahmad Reza .

RSC ADVANCES, 2016, 6 (76) :72777-72790

[4] High sulfur loaded carbon aerogel cathode for lithium-sulfur batteries [J].

Balakumar, K. ;

Kalaiselvi, N. .

RSC ADVANCES, 2015, 5 (43) :34008-34018

[5] Control of average particle size of carbon aerogel supported platinum nanoparticles by supercritical deposition [J].

Barim, Sansim Bengisu ;

Bayrakceken, Ayse ;

Bozbag, Semi Erim ;

Zhang, Lichun ;

Kizilel, Riza ;

Aindow, Mark ;

Erkey, Can .

MICROPOROUS AND MESOPOROUS MATERIALS, 2017, 245 :94-103

[6] THERMAL-PROPERTIES OF CARBON AEROGELS [J].

BOCK, V ;

NILSSON, O ;

BLUMM, J ;

FRICKE, J .

JOURNAL OF NON-CRYSTALLINE SOLIDS, 1995, 185 (03) :233-239

[7] Ultralow density carbon aerogels with low thermal conductivity up to 2000 °C [J].

Feng, Junzong ;

Feng, Jian ;

Jiang, Yonggang ;

Zhang, Changrui .

MATERIALS LETTERS, 2011, 65 (23-24) :3454-3456

[8] 3D hierarchical porous N-doped carbon aerogel from renewable cellulose: an attractive carbon for high-performance supercapacitor electrodes and CO2 adsorption [J].

Hu, Yijie ;

Tong, Xing ;

Zhuo, Hao ;

Zhong, Linxin ;

Peng, Xinwen ;

Wang, Sha ;

Sun, Runcang .

RSC ADVANCES, 2016, 6 (19) :15788-15795

[9]

Hüsing N, 1998, ANGEW CHEM INT EDIT, V37, P23, DOI 10.1002/(SICI)1521-3773(19980202)37:1/2<22::AID-ANIE22>3.0.CO

[10]

2-I

← 1 2 3 →