Effects of Heat Treating Silane and Different Etching Techniques on Glass Fiber Post Push-out Bond Strength

The aims of this study were to compare two pretreatment methods of a fiber post and to evaluate the effect of heat treatment to applied silane on the push-out bond strength for different levels of root. In this in vitro study, 40 glass fiber posts were divided into five groups (n=8) according to the kind of surface treatment applied. They were then inserted into extracted and endodontically treated human canines using a self-etch resin cement (Panavia F2.0, Kuraray, Japan). Group HF+S = hydrofluoric acid (HF) etching and silane (S) application; group HF+S+WP = HF etching and heat-treated silane application and warmed posts (WP); group H-2 O-2+S = hydrogen peroxide etching and silane application; group H-2 O-2 +S+WP = hydrogen peroxide and heattreated- silane application and warmed post; and group C, the control group, received no pretreatment. After completion of thermal cycling (1000 cycles, 5-55 degrees C), all specimens were cut horizontally to obtain three sections. Each section was subjected to a push-out test, and the test results were analyzed using two-way analysis of variance, post-hoc Tukey honestly significant difference test, and a paired sample t-test (alpha= 0.05). It was found that bond strength was not statistically influenced by the kind of etching material used (p= 0.224), but was significantly affected by heat treatment of applied silane (p < 0.001). The interaction between these two factors was not statistically significant (p= 0.142). Group HF+S+WP showed the highest bond strength (12.5661.73 MPa) (p < 0.05). Scanning electron microscopy revealed the effect of the different treatments on the surface characteristics of posts. In the four pretreated groups, the bond strength decreased significantly from the coronal to the apical root canal sections (p <= 0.05). The results of this study show that the use of heat treated silane significantly enhances the pushout bond strength of the fiber posts to root. HF acid etching with heat-treated silane application led to the highest bond strength.