A method for investigation of hot corrosion by gaseous Na2SO4

被引：23
作者：
Knutsson, Pavleta [1 ]
Lai, Haiping [1 ]
Stiller, Krystyna [1 ]
机构：
[1] Chalmers Univ Technol, Dept Appl Phys, S-41296 Gothenburg, Sweden
来源：
CORROSION SCIENCE | 2013年 / 73卷
关键词：
Hot corrosion; Superalloy; Sulfidation; SEM; XPS; HIGH-TEMPERATURE CORROSION; COATINGS; BEHAVIOR; ALLOYS;
D O I：
10.1016/j.corsci.2013.04.006
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A novel in situ exposure method for investigating hot corrosion of aluminde coatings in the absence of an alkali sulphate melt is presented. The samples are exposed to Na2SO4(g) at a temperature above the dew point of the gas. Results from 100 and 500 h exposures at 900 degrees C of Ni-based In792 covered with SIF232 aluminide coating are presented. Already after 100 h of testing, attack characteristic for Type I hot corrosion is observed. The reactions taking place during the testing are discussed and the results are compared with those from the well-known ex situ salt hot corrosion test. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：230 / 236
页数：7
相关论文
共 50 条
  • [21] Hot corrosion of modified Ti3Al-based alloy coated with thin Na2SO4 film at 910 and 950°C in air
    Qian, Yu-hai
    Li, Xi-chao
    Li, Mei-shuan
    Xu, Jing-jun
    Lu, Bin
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2017, 27 (04) : 954 - 961
  • [22] Hot corrosion behavior of network structured TiBw/TA15 composite with Na2SO4 film at 800?C
    Kang, Qingxin
    Xu, Xiaoting
    Wang, Guofeng
    Luo, Shuyi
    Zhan, Liqiang
    MATERIALS CHARACTERIZATION, 2023, 195
  • [23] Hot corrosion behavior of AlCuFeCr quasicrystalline coating on titanium alloy with the mixture of NaCl and Na2SO4 deposit
    Wang, Fengfeng
    Zhou, Chungen
    Gong, Shengkai
    Xu, Huibin
    2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM, 2007, 546-549 : 2313 - +
  • [24] Assessment of Hot Corrosion in Molten Na2SO4 and V2O5 of Inconel 625 Fabricated by Selective Laser Melting versus Conventional Technology
    Badea, Teodor Adrian
    Batalu, Dan
    Constantin, Nicolae
    Paraschiv, Alexandru
    Patroi, Delia
    Ceatra, Laurentiu Constantin
    MATERIALS, 2022, 15 (12)
  • [25] Hot corrosion behaviour of Nbss/Nb5Si3 in situ composites in the mixture of Na2SO4 and NaCl melts
    Wang, Wan
    Zhou, Chungen
    CORROSION SCIENCE, 2013, 74 : 345 - 352
  • [26] Hot corrosion behavior and near-surface microstructure of a "low-temperature high-activity Cr-aluminide" coating on inconel 738LC exposed to Na2SO4, Na2SO4 + V2O5 and Na2SO4 + V2O5 + NaCl at 900 °C
    Doolabi, M. Salehi
    Ghasemi, B.
    Sadrnezhaad, S. K.
    Habibollahzadeh, A.
    Jafarzadeh, K.
    CORROSION SCIENCE, 2017, 128 : 42 - 53
  • [27] Severe Hot Corrosion of the Superalloy IN718 in Mixed Salts of Na2SO4 and V2O5 at 700 °C
    Pradhan, Dhananjay
    Mahobia, Girija Shankar
    Chattopadhyay, Kausik
    Singh, Vakil
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2018, 27 (08) : 4235 - 4243
  • [28] Evaluation of hot corrosion performance of HVOF coatings on PCGTA welded Fe-based alloy A-286 in Na2SO4%-7.5%NaVO3%-5%NaCl environment
    Muthu, S. M.
    Arivarasu, M.
    SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES, 2020, 8 (04):
  • [29] Hot Corrosion Behavior of Hf-Doped NiAl Coating in the Mixed Salt of Na2SO4 + K2SO4 at 900 °C
    Zhang, W. L.
    Li, W.
    Fu, L. B.
    Peng, X.
    Sun, J.
    Jiang, S. M.
    Gong, J.
    Sun, C.
    ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2023, 36 (09) : 1409 - 1420
  • [30] Hot Corrosion Behavior of Hf-Doped NiAl Coating in the Mixed Salt of Na2SO4 + K2SO4 at 900 °C
    W. L. Zhang
    W. Li
    L. B. Fu
    X. Peng
    J. Sun
    S. M. Jiang
    J. Gong
    C. Sun
    Acta Metallurgica Sinica (English Letters), 2023, 36 : 1409 - 1420
12345