A method for investigation of hot corrosion by gaseous Na2SO4

被引：23
|
作者：
Knutsson, Pavleta [1 ]
Lai, Haiping [1 ]
Stiller, Krystyna [1 ]
机构：
[1] Chalmers Univ Technol, Dept Appl Phys, S-41296 Gothenburg, Sweden
来源：
CORROSION SCIENCE | 2013年 / 73卷
关键词：
Hot corrosion; Superalloy; Sulfidation; SEM; XPS; HIGH-TEMPERATURE CORROSION; COATINGS; BEHAVIOR; ALLOYS;
D O I：
10.1016/j.corsci.2013.04.006
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A novel in situ exposure method for investigating hot corrosion of aluminde coatings in the absence of an alkali sulphate melt is presented. The samples are exposed to Na2SO4(g) at a temperature above the dew point of the gas. Results from 100 and 500 h exposures at 900 degrees C of Ni-based In792 covered with SIF232 aluminide coating are presented. Already after 100 h of testing, attack characteristic for Type I hot corrosion is observed. The reactions taking place during the testing are discussed and the results are compared with those from the well-known ex situ salt hot corrosion test. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：230 / 236
页数：7
相关论文
共 50 条
  • [1] Hot corrosion behavior of SiC in molten Na2SO4
    Nakagawa, T
    Hara, M
    Imai, K
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1997, 61 (11) : 1241 - 1248
  • [2] Hot corrosion of the Ni-20%Cr alloy and waspaloy immersed in Na2SO4
    Kusabiraki, Kiyoshi
    Morita, Masashi
    Guo, Xiping
    Anada, Hiroshi
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2007, 93 (07): : 498 - 505
  • [3] Comparison of Na2SO4, K2SO4 and Na2SO4-K2SO4 deposit induced hot corrosion of a β-NiAl coating
    Wang, Yaping
    Pillai, Rishi
    Yazhenskikh, Elena
    Frommherz, Martin
    Mueller, Michael
    Quadakkers, Willem Joseph
    Naumenko, Dmitry
    CORROSION SCIENCE, 2022, 198
  • [4] Hot corrosion behavior of CM 247 LC alloy in Na2SO4 and NaCl environments
    Gurrappa, I
    OXIDATION OF METALS, 1999, 51 (5-6): : 353 - 382
  • [5] Hot Corrosion Behavior of CM 247 LC Alloy in Na2SO4 and NaCl Environments
    I. Gurrappa
    Oxidation of Metals, 1999, 51 : 353 - 382
  • [6] Corrosion behavior of the NiCrAlY and NiSiAlY alloys with salt mixtures of NaCl/Na2SO4
    Zheng, Haiyang
    Cui, Tiancheng
    Zhu, Bing
    Yu, Xiaopeng
    Yu, Miao
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A, 2024, 42 (02):
  • [7] Hot Corrosion of Co-based Alloys with 25%NaCl+75%Na2SO4 Coating at 1173 K
    Fu, Guangyan
    Guo, Xingxing
    Liu, Qun
    Zhao, Xin
    Su, Yong
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2013, 32 (03) : 317 - 321
  • [8] Comparison investigation of hot corrosion exposed to Na2SO4 salt and oxidation of MoSi2-based coating on Nb alloy at 1000 °C
    Sun, Le
    Fu, Qian-Gang
    Sun, Jia
    Zhang, Guang-peng
    SURFACE & COATINGS TECHNOLOGY, 2020, 385 (385)
  • [9] Na2SO4 Induced Hot Corrosion of Aluminized Low Carbon Steel at 700 °C
    Badaruddin, Mohammad
    ADVANCES IN APPLIED MECHANICS AND MATERIALS, 2014, 493 : 761 - 766
  • [10] Hot Corrosion Behavior of ZrB2-SiC-Graphite Composite in NaCl and Na2SO4 Molten Salts
    Liu, X.
    Wang, G.
    Liu, L.
    Wang, Z.
    Wu, Z.
    Liu, M.
    JOURNAL OF CERAMIC SCIENCE AND TECHNOLOGY, 2018, 9 (03): : 309 - 317
12345