Study of Flame-retardant and Waterproof Breathable Fabric by Coating Finishing

被引：0

作者：

Gu, Yannan ^{[1
]}

Zheng, Jinhuan ^{[1
]}

Chen, Yangyi ^{[1
]}

机构：

[1] Zhejiang Sci Tech Univ, Minist Educ China, Key Lab Adv Text Mat & Mfg Technol, Hangzhou 310018, Peoples R China

来源：

ADVANCED MATERIALS AND PROCESSES II, PTS 1-3 | 2012年 / 557-559卷

关键词：

Flame retardancy; Moisture quantity; Water pressure resistance; Coating;

D O I：

10.4028/www.scientific.net/AMR.557-559.1964

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Organic flame retardant of N-P complex type and inorganic flame retardant hydrotalcite were respectively added to waterproof breathable coating agent,the influence of dosages of two flame retardants on the flame retardancy of coated fabric were studied,and the influence of the optimal dosages of different flame retardants on the waterproof breathable permeability of coated fabric were investigated. The results show that adding inorganic flame retardant hydrotalcite has better flame-retardant and waterproof breathable permeability when the addition of hydrotalcite is 5% quality of coating agent, after-flame time and after-glow time of coated fabric are 0s, char length is 10.5cm, moisture quantity is 7247g/m(2).24h, water pressure resistance is 430mmH(2)O.

引用

页码：1964 / 1970

页数：7

共 8 条

[1]

[范惠琳 Fan Huilin], 2011, [工程塑料应用, The Journal of Engineering Plastics Application], V39, P10

[2]

Giessmann A, 1998, J COATED FABRICS, V28, P56

[3]

Huang Jie, 2009, CHINA PLASTICS, V4, P71

[4]

Li Jie, 2005, SILK, V2, P40

[5]

[潘云芳 Pan Yunfang], 2004, [纺织学报, Journal of Textile Research], V25, P94

[6] Thermal behaviour of covalently bonded phosphate and phosphonate flame retardant polystyrene systems [J].

Price, Dennis ;

Cunliffe, L. K. ;

Bullett, K. J. ;

Hull, T. R. ;

Milnes, G. J. ;

Ebdon, J. R. ;

Hunt, B. J. ;

Joseph, P. .

POLYMER DEGRADATION AND STABILITY, 2007, 92 (06) :1101-1114

[7]

Zhao Yaping, 2010, PRINTING DYEING, V15, P1

[8]

Zhuo Qiqi, 2010, POLYVINYL ALCOHOL HY

← 1 →