Failure bending stresses for pressurized pipes with circumferentially part-through cracks

Stress corrosion cracks detected in austenitic stainless pipes were circumferential cracks at inside of the pipes. Failure stresses for the cracked pipes were developed by net-section stress concept. Limit Load Criterion provided by the ASME Code based on the net-section stress concept can estimate fully plastic collapse stress, which is called as failure stress. Local Approach of Limit Load Criteria for estimating stress at crack penetration had developed for a part-through cracked pipe based on the Limit Load Criteria. Advanced Local Approach of Limit Load Criteria for estimating stress at crack penetration is newly developed based on the Local Approach in this paper. In comparing with experimental stresses of pipe crack penetrations, the Limit Load Criteria give unconservative estimation, and the Local and the Advanced Local Approaches are close to the experimental stresses. In addition, the Advanced Local Approach always gives higher stresses than the Local Approach for internal cracks, and it is shown that the Advanced Local Approach is beneficial for thick wall pipes with large angle cracks.