Magnetic structure of Fe16N2 determined by polarized neutron diffraction on thin-film samples

被引：14

作者：

Hang, Xudong ^{[1
]}

Matsuda, Masaaki ^{[2
]}

Held, Jacob T. ^{[1
]}

Mkhoyan, K. Andre ^{[1
]}

Wang, Jian-Ping ^{[1
,3
]}

机构：

[1] Univ Minnesota, Dept Chem Engn & Mat Sci, Minneapolis, MN 55455 USA

[2] Oak Ridge Natl Lab, Neutron Scattering Div, Oak Ridge, TN 37831 USA

[3] Univ Minnesota, Dept Elect & Comp Engn, Minneapolis, MN 55455 USA

来源：

PHYSICAL REVIEW B | 2020年 / 102卷 / 10期

关键词：

SINGLE-CRYSTAL FE16N2; MOMENT; NITRIDE;

D O I：

10.1103/PhysRevB.102.104402

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Strain-free Fe16N2 thin films were obtained on MgO (001) single-crystal substrates with Cr seed layers. X-ray diffraction and transmission electron microscopy confirmed that the film is textured in all three spatial directions with crystallographic orientation determined by epitaxial constraints from the substrate. Average grain size was estimated to be in the range of tens of nanometers. Ten pieces of 40-nm-thick Fe16N2 thin-film samples were stacked together for half-polarized neutron diffraction study at room temperature. A total of six reflections were usable, from which the magnetic structure of Fe16N2 was determined and compared to existing models. Contrary to most electronic structure calculations, the present results suggest that the magnetic moment of Fe atoms at the 8h site is large and larger than that of the 4d site. Our results support the giant magnetization of Fe16N2.