Effect of plasma electrolytic oxidation treatment on the corrosion and stress corrosion cracking behaviour of AM50 magnesium alloy

被引:71
作者
Srinivasan, P. Bala [1 ]
Blawert, C. [1 ]
Dietzel, W. [1 ]
机构
[1] GKSS Forschungszentrum Geesthacht GmbH, Inst Mat Res, D-21502 Geesthacht, Germany
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2008年 / 494卷 / 1-2期
关键词
Magnesium alloy; Plasma electrolytic oxidation; Electrochemical behaviour; Stress corrosion cracking; Fractography;
D O I
10.1016/j.msea.2008.04.031
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The effect of a silicate-based plasma anodization treatment on the corrosion and stress corrosion cracking behaviour of a cast AM50 magnesium alloy was studied. Electrochemical tests revealed the beneficial effect of the plasma electrolytic oxidation (PEO) in improving the corrosion resistance of the alloy. Although the coating had provided an improved resistance to stress corrosion cracking in this test environment at a nominal strain rate of 10(-6) s(-1), it could not completely eliminate the SCC susceptibility of the alloy. Cracking of the coating under conditions of straining was found to be the reason for SCC of PEO-coated alloy. (C) 2008 Elsevier B.V. All Fights reserved.
引用
收藏
页码:401 / 406
页数:6
相关论文
共 50 条
[31]   Enhancing corrosion resistance of plasma electrolytic oxidation coatings on AM50 Mg alloy by inhibitor containing Ba(NO3)2 solutions [J].
Ma, Jirui ;
Lu, Xiaopeng ;
Sah, Santosh Prasad ;
Chen, Qianqian ;
Zhang, You ;
Wang, Fuhui .
INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2024, 31 (09) :2048-2061
[32]   Environmental friendly plasma electrolytic oxidation of AM60 magnesium alloy and its corrosion resistance [J].
曹发和 ;
林龙勇 ;
张昭 ;
张鉴清 ;
曹楚南 .
Transactions of Nonferrous Metals Society of China, 2008, (02) :240-247
[33]   Environmental friendly plasma electrolytic oxidation of AM60 magnesium alloy and its corrosion resistance [J].
Cao Fa-he ;
Lin Long-yong ;
Zhang Zhao ;
Zhang Jian-qing ;
Cao Chu-nan .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2008, 18 (02) :240-247
[34]   Environmentally assisted cracking behaviour of plasma electrolytic oxidation coated AZ31 magnesium alloy [J].
Srinivasan, P. Bala ;
Liang, J. ;
Blawert, C. ;
Dietzel, W. .
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2011, 46 (06) :706-711
[35]   Wear and corrosion behavior of clay containing coating on AM 50 magnesium alloy produced by aluminate-based plasma electrolytic oxidation [J].
Davoodi, Farideh ;
Atapour, Masoud ;
Blawert, Carsten ;
Zheludkevich, Mikhail .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2021, 31 (12) :3719-3738
[36]   Microstructure and corrosion resistant property of laser surface melting layer of AM50 magnesium alloy [J].
School of Mechanical Engineering, Jiangsu University, Zhenjiang 212013, China ;
不详 .
Zhongguo Jiguang, 2008, 2 (307-310) :307-310
[37]   Corrosion degradation of AZ31 magnesium alloy coated by plasma electrolytic oxidation [J].
Kajanek, Daniel ;
Hadzima, Branislav ;
Buhagiar, Joseph ;
Wasserbauer, Jaromir ;
Jackova, Martina .
13TH INTERNATIONAL SCIENTIFIC CONFERENCE ON SUSTAINABLE, MODERN AND SAFE TRANSPORT (TRANSCOM 2019), 2019, 40 :51-58
[38]   In Situ Construction of Fluorescent and Corrosion Resistant Coating by Plasma Electrolytic Oxidation on Magnesium Alloy [J].
Qiu, Zhaozhong ;
Liu, Bojun ;
Sun, Jia ;
Wang, Rui ;
Limei, Sun .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2025, 34 (06) :4680-4688
[39]   Fatigue Behavior of an AM50 Die-Casting Alloy Anodized by Plasma Electrolytic Oxidation [J].
Choi, Kwangmin ;
Kang, Seungwon ;
Kang, Heon .
MATERIALS, 2021, 14 (24)
[40]   CHARACTERIZATION OF CORROSION AND STRESS CORROSION CRACKING OF AE44 MAGNESIUM ALLOY [J].
Sozanska, M. ;
Moscicki, A. ;
Chmiela, B. .
ARCHIVES OF METALLURGY AND MATERIALS, 2020, 65 (01) :479-484