Synthesis and Characterization of Sol-Gel Alumina Fiber by Seeding α-Alumina Through Extended Ball Milling

被引：11

作者：

Chandradass, J. ^{[1
,3
]}

Bae, Dong Sik ^{[3
]}

Balasubramanian, M. ^{[1
,2
]}

机构：

[1] Indian Inst Technol, Composites Technol Ctr, Madras 600036, Tamil Nadu, India

[2] Indian Inst Technol, Dept Met & Mat Engn, Madras 600036, Tamil Nadu, India

[3] Changwon Natl Univ, Sch Nano & Adv Mat Engn, Nanopowder Proc & Synth Lab, Chang Won, Gyeongnam, South Korea

来源：

MATERIALS AND MANUFACTURING PROCESSES | 2008年 / 23卷 / 08期

关键词：

Al2O3; Fibers; Grain size; Mechanical properties; Microstructure; SEM; Sintering; Sol-gel processes; Strength; Thermal analysis; X-ray diffraction;

D O I：

10.1080/10426910802382098

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Alumina fibers were prepared by sol-gel process using alpha-Al2O3 seeded boehmite sol. The starting material used for the preparation of boehmite sol was aluminium-tri-isopropoxide. Extended ball milling of boehmite sol using alumina grinding media was carried out to incorporate nucleating seeds of alpha-Al2O3 to boehmite sol. Differential thermal analysis showed that the phase transition to alpha-Al2O3 takes place at a much lower temperature by seeding alpha-Al2O3. The presence of alpha-Al2O3 seeds decreases the sintering temperature and a relatively dense microstructure with very fine grain size is formed at 1300 degrees C. The fibers sintered at 1300 degrees C have the highest tensile strength.

引用

页码：786 / 790

页数：5

共 25 条

[1] Fine diameter ceramic fibres [J].

Bunsell, AR ;

Berger, MH .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2000, 20 (13) :2249-2260

[2] SINTERING AND GRAIN GROWTH OF ALPHA-ALUMINA [J].

CAHOON, HP ;

CHRISTENSEN, CJ .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1956, 39 (10) :337-344

[3] Zirconia fibre mats prepared by a sol-gel spinning technique [J].

Chakrabarty, PK ;

Chatterjee, M ;

Naskar, MK ;

Siladitya, B ;

Ganguli, D .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2001, 21 (03) :355-361

[4] Extrusion of alumina fibre using sol-gel precursor [J].

Chandradass, J. ;

Balasubramanian, M. .

JOURNAL OF MATERIALS SCIENCE, 2006, 41 (18) :6026-6030

[5] Sol-gel based extrusion of alumina fibers [J].

Chandradass, J. ;

Balasubramanian, M. .

MATERIALS AND MANUFACTURING PROCESSES, 2006, 21 (03) :319-323

[6] Sol-gel processing of alumina fibres [J].

Chandradass, J ;

Balasubramanian, M .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2006, 173 (03) :275-280

[7] Mullite fibre mats by a sol-gel spinning technique [J].

Chatterjee, M ;

Naskar, MK ;

Chakrabarty, PK ;

Ganguli, D .

JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2002, 25 (02) :169-174

[8] Mechanical properties of alumina Nextel™ 720 fibres at room and elevated temperatures:: tensile bundle testing [J].

Dassios, KG ;

Steen, M ;

Filiou, C .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 349 (1-2) :63-72

[9] Microstructural stability and room temperature mechanical properties of the Nextel 720 fibre [J].

Deléglise, F ;

Berger, MH ;

Jeulin, D ;

Bunsell, AR .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2001, 21 (05) :569-580

[10]

DYNYS FD, 1984, ALPHA ALUMINA FORMAT

← 1 2 3 →