Preparation and properties of electroless Ni-Zn-P alloy films

被引：28
作者：
Oulladj, M
Saidi, D
Chassaing, E
Lebaili, S
机构：
[1] Ctr Dev Mat, Met Lab, Alger 16000, Algeria
[2] CNRS, Ctr Etud Chim Met, F-94407 Vitry, France
[3] USTHB, Inst Genie Mecan, Alger, Algeria
来源：
JOURNAL OF MATERIALS SCIENCE | 1999年 / 34卷 / 10期
关键词：
Sodium; Polymer; Chloride; Sodium Chloride; Chloride Solution;
D O I：
10.1023/A:1004566817439
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Electroless deposition of Ni-Zn-P layers was studied on steel electrodes by varying the bath temperature (40-90 degrees C), pH and chemical composition. The deposition parameters were optimized. Alloys containing 70-86 wt % Ni, 6-20 wt % Zn and 6-10 wt % P are obtained at 20 mu m h(-1) and 85 degrees C. Corrosion measurements were performed in aerated 5% sodium chloride solution, the corrosion potential and current density are, respectively, -0.49 V/SCE and 2.6 mu A cm(-2). (C) 1999 Kluwer Academic Publishers.
引用
收藏
页码：2437 / 2439
页数：3
相关论文
共 17 条
[1]  
AOKA K, 1995, JPN, V46, P79
[2]   ELECTROLYTIC NI-PB-P ALLOYS [J].
BIELINSKI, J ;
BIELINSKA, A .
SURFACE TECHNOLOGY, 1985, 24 (03) :219-231
[3]  
Brenner A., 1963, ELECTRODEPOSITION AL, V2
[4]  
Brenner A., 1963, ELECTRODEPOSITION AL, V1
[5]  
BRUNET R, 1985, THESIS U P M CURIE P
[6]  
CHERKAOUI M, 1992, PLAT SURF FINISH, P68
[7]  
LUSTMAN B, 1943, T ELECTROCHEM SOC, V84, P363
[8]   ELECTROLESS COPPER PLATING FROM AN IMINODIACETATE BATH [J].
OHNO, I .
SURFACE TECHNOLOGY, 1976, 4 (06) :515-520
[9]  
Paunovic M., 1968, PLATING, V55, P1161
[10]  
PECHERSKAYA AG, 1950, ZH PRIKL KHIM, V23, P920
12