A low temperature internal friction study of Y0.85Ca0.15Ba2Cu3O7-δ with different oxygen content

被引：6

作者：

Ying, XN ^{[1
]}

He, J

Wang, YN

机构：

[1] Nanjing Univ, Natl Lab Solid State Microstruct, Nanjing 210093, Peoples R China

[2] Nanjing Univ, Dept Phys, Nanjing 210093, Peoples R China

来源：

SOLID STATE COMMUNICATIONS | 2004年 / 130卷 / 07期

关键词：

high-temperature superconductors; ultrasonics;

D O I：

10.1016/j.ssc.2004.03.002

中图分类号：

O469 [凝聚态物理学];

学科分类号：

070205 ;

摘要：

The ceramic sample of Y0.85Ca0.15BaCu3O7-delta was prepared by standard solid-state reaction method, and samples with different oxygen concentration were obtained by quenching from high temperature. The internal friction was measured using the vibrating reed method from liquid-nitrogen temperature to room temperature at kilohertz frequency. An internal friction peak was observed around 250 K in Y0.85Ca0.15BaCu3O7-delta quenched from 1023 K. The peak is related to the one observed around 220 K (labeled as P3 peak) in uricloped YBa2Cu3O7-delta (Y 123). This result shows the dependence of P3 peak on carriers density and P3 peak has a strong correlation to the abnormal behavior of Y123 in the underdoped range. The variation of two low temperature thermal activated relaxation peaks (P1 and P2) on oxygen content were also investigated. And consistent explanations were given based on all recent researches. (C) 2004 Elsevier Ltd. All rights reserved.

引用

页码：441 / 444

页数：4

共 20 条

[1] Evidence for a structural change in TSMG Y123 at 225 K [J].

Anderson, AR ;

Murakami, M ;

Nagashima, K ;

Russell, GJ .

PHYSICA C, 1998, 306 (1-2) :15-20

[2] HOW NQR CONTRIBUTES TO THE UNDERSTANDING OF HIGH-TEMPERATURE SUPERCONDUCTORS [J].

BRINKMANN, D .

JOURNAL OF MOLECULAR STRUCTURE, 1995, 345 :167-172

[3] DYNAMICS OF OXYGEN AND PHASE-TRANSITIONS IN THE 123 CERAMIC SUPERCONDUCTORS BY ANELASTIC RELAXATION MEASUREMENTS [J].

CANNELLI, G ;

CANTELLI, R ;

CORDERO, F ;

TREQUATTRINI, F .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1992, 5 (04) :247-257

[4]

CHEN CF, 1988, PHYSICA B & C, V147, P175

[5] EFFECTS OF SUBSTITUTING CALCIUM FOR YTTRIUM ON THE PROPERTIES OF YBA2CU3O7-DELTA [J].

FISHER, B ;

GENOSSAR, J ;

KUPER, CG ;

PATLAGAN, L ;

REISNER, GM ;

KNIZHNIK, A .

PHYSICAL REVIEW B, 1993, 47 (10) :6054-6059

[6]

Gridnev S. A., 1993, Ferroelectrics, V144, P107, DOI 10.1080/00150199308008632

[7] FACTORS INFLUENCING TC IN 123 COPPER-OXIDE SUPERCONDUCTORS [J].

MANTHIRAM, A ;

GOODENOUGH, JB .

PHYSICA C, 1989, 159 (06) :760-768

[8] Two crossovers in the pseudogap regime of YBa2Cu3O7-δ superconductors observed by ultrafast spectroscopy -: art. no. 067002 [J].

Misochko, OV ;

Georgiev, N ;

Dekorsy, T ;

Helm, M .

PHYSICAL REVIEW LETTERS, 2002, 89 (06)

[9] Large, Small, and Especially Jahn–Teller Polarons [J].

K. A. M¨ller .

Journal of Superconductivity, 1999, 12 (1) :3-7

[10] The ratio of small polarons to free carriers in La2-xSrxCuO4 derived from susceptibility measurements [J].

Muller, KA ;

Zhao, GM ;

Conder, K ;

Keller, H .

JOURNAL OF PHYSICS-CONDENSED MATTER, 1998, 10 (18) :L291-L296

← 1 2 →