Structural and Optical Properties of Glancing Angle Deposited TiO2 Nanowires Array

被引：13

作者：

Chinnamuthu, P. ^{[1
]}

Mondal, A. ^{[1
]}

Singh, N. K. ^{[1
]}

Dhar, J. C. ^{[1
]}

Das, S. K. ^{[2
]}

Chattopadhyay, K. K. ^{[3
]}

机构：

[1] Natl Inst Technol Agartala, Dept Elect & Commun Engn, Jirania 799055, Tripura West, India

[2] Univ Calcutta, Dept Elect Sci, Kolkata 700009, India

[3] Jadavpur Univ, Dept Phys, Kolkata 700032, India

来源：

JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY | 2012年 / 12卷 / 08期

关键词：

GLAD; TiO2; Nanowire; FE-SEM; HR-TEM; Photoluminescence; Optical Absorption; SENSITIZED SOLAR-CELLS; GROWTH; FILMS; TRANSITION; NANORODS; OXIDES; ZNO;

D O I：

10.1166/jnn.2012.6455

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

TiO2 nanowires (NWs) have been synthesized by glancing angle deposition technique using e-beam evaporator. The average length 490 nm and diameter 80 nm of NWs were examined by field emission-scanning electron microscopy. Transmission electron microscopy emphasized that the NWs were widely dispersed at the top. X-ray diffraction has been carried out on the TiO2 thin film (TF) and NW array. A small blue shift of 0.03 eV was observed in Photoluminescence (PL) main band emission for TiO2 NW as compared to TiO2 TF. The high temperature annealing at 980 degrees C partially removed the oxygen vacancy from the sample, which was investigated by PL and optical absorption measurements.

引用

页码：6445 / 6448

页数：4

共 24 条

[1] Nanowire-based dye-sensitized solar cells [J].

Baxter, JB ;

Aydil, ES .

APPLIED PHYSICS LETTERS, 2005, 86 (05) :1-3

[2] Growth and characterization of well-aligned densely-packed rutile TiO2 nanocrystals on sapphire substrates via metal-organic chemical vapor deposition [J].

Chen, C. A. ;

Chen, Y. M. ;

Korotcov, A. ;

Huang, Y. S. ;

Tsai, D. S. ;

Tiong, K. K. .

NANOTECHNOLOGY, 2008, 19 (07)

[3] Ultraviolet detection using TiO2 nanowire array with Ag Schottky contact [J].

Chinnamuthu, P. ;

Dhar, J. C. ;

Mondal, A. ;

Bhattacharyya, A. ;

Singh, N. K. .

JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2012, 45 (13)

[4] Photoactive and antibacterial TiO2 thin films on stainless steel [J].

Evans, P. ;

Sheel, D. W. .

SURFACE & COATINGS TECHNOLOGY, 2007, 201 (22-23) :9319-9324

[5] Vertically Aligned Single Crystal TiO2 Nanowire Arrays Grown Directly on Transparent Conducting Oxide Coated Glass: Synthesis Details and Applications [J].

Feng, Xinjian ;

Shankar, Karthik ;

Varghese, Oomman K. ;

Paulose, Maggie ;

Latempa, Thomas J. ;

Grimes, Craig A. .

NANO LETTERS, 2008, 8 (11) :3781-3786

[6]

GOTO M, 2006, 28 INT C PHYS SEM IC

[7] General route to vertical ZnO nanowire arrays using textured ZnO seeds [J].

Greene, LE ;

Law, M ;

Tan, DH ;

Montano, M ;

Goldberger, J ;

Somorjai, G ;

Yang, PD .

NANO LETTERS, 2005, 5 (07) :1231-1236

[8] Optical and photocatalytic properties of oblique angle deposited TiO2 nanorod array [J].

He, Y. P. ;

Zhang, Z. Y. ;

Zhao, Y. P. .

JOURNAL OF VACUUM SCIENCE & TECHNOLOGY B, 2008, 26 (04) :1350-1358

[9]

Henrich V. E., 1994, SURFACE SCI METAL OX

[10] Growth of submicrometer-scale rectangular parallelepiped rutile TiO2 films in aqueous TiCl3 solutions under hydrothermal conditions [J].

Hosono, E ;

Fujihara, S ;

Kakiuchi, K ;

Imai, H .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2004, 126 (25) :7790-7791

← 1 2 3 →