A redox responsive polymeric gel based on ionic crosslinking

被引:28
作者
Fei, Shih-To
Phelps, Mwita V. B.
Wang, Yang
Barrett, Eric
Gandhi, Farhan
Allcock, Harry R. [1 ]
机构
[1] Penn State Univ, Dept Chem, University Pk, PA 16802 USA
[2] Penn State Univ, Dept Aerosp Engn, University Pk, PA 16802 USA
关键词
D O I
10.1039/b516972k
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
We report here an electrochemically responsive polymer hydrogel based on ionic crosslinking. The crosslinking by metal cations and anionic carboxylic acid side groups can be controlled by redox reactions. The crosslinks dissociate when the cation crosslinker is reduced to a lower oxidation state and reform following oxidation, which leads to a reversible and localized swelling-contraction. By choosing biocompatible components and miniaturization designs, the system has potential in microrobotic and biomedical applications.
引用
收藏
页码:397 / 401
页数:5
相关论文
共 17 条
[1]   HYDROPHILIC POLYPHOSPHAZENES AS HYDROGELS - RADIATION CROSS-LINKING AND HYDROGEL CHARACTERISTICS OF POLY[BIS(METHOXYETHOXYETHOXY)PHOSPHAZENE] [J].
ALLCOCK, HR ;
KWON, S ;
RIDING, GH ;
FITZPATRICK, RJ ;
BENNETT, JL .
BIOMATERIALS, 1988, 9 (06) :509-513
[2]   AN IONICALLY CROSS-LINKABLE POLYPHOSPHAZENE - POLY[BIS(CARBOXYLATOPHENOXY)PHOSPHAZENE] AND ITS HYDROGELS AND MEMBRANES .8. [J].
ALLCOCK, HR ;
KWON, S .
MACROMOLECULES, 1989, 22 (01) :75-79
[3]   Lower critical solubility temperature study of alkyl ether based polyphosphazenes [J].
Allcock, HR ;
Dudley, GK .
MACROMOLECULES, 1996, 29 (04) :1313-1319
[4]   Controlled formation of carboxylic acid groups at polyphosphazene surfaces: Oxidative and hydrolytic routes [J].
Allcock, HR ;
Morrissey, CT ;
Way, WK ;
Winograd, N .
CHEMISTRY OF MATERIALS, 1996, 8 (12) :2730-2738
[5]   Synthesis and characterization of pH-sensitive poly(organophosphazene) hydrogels [J].
Allcock, HR ;
Ambrosio, AMA .
BIOMATERIALS, 1996, 17 (23) :2295-2302
[6]  
Bar-Cohen Y, 1999, P SPIES EL POL ACT D, V3669, P1
[7]   Dielectric properties of relaxor-like vinylidene fluoride - Trifluoroethylene-based electroactive polymers [J].
Bobnar, V ;
Vodopivec, B ;
Levstik, A ;
Kosec, M ;
Hilczer, B ;
Zhang, QM .
MACROMOLECULES, 2003, 36 (12) :4436-4442
[8]   Electrostrictive properties of poly(vinylidenefluoridetrifluoroethylene-chlorotrifluoroethylene) [J].
Buckley, GS ;
Roland, CM ;
Casalini, R ;
Petchsuk, A ;
Chung, TC .
CHEMISTRY OF MATERIALS, 2002, 14 (06) :2590-2593
[9]   REDOX CAPACITY AND DIRECT-CURRENT ELECTRON CONDUCTIVITY IN ELECTROACTIVE MATERIALS [J].
CHIDSEY, CED ;
MURRAY, RW .
JOURNAL OF PHYSICAL CHEMISTRY, 1986, 90 (07) :1479-1484
[10]   Microfabricating conjugated polymer actuators [J].
Jager, EWH ;
Smela, E ;
Inganäs, O .
SCIENCE, 2000, 290 (5496) :1540-1545