Proton conduction in perovskite oxide BaZr0.5Yb0.5O3-δ prepared by wet chemical synthesis route

被引：16

作者：

Ahmed, Istaq ^{[1
]}

Knee, Christopher S. ^{[2
]}

Eriksson, Sten-Gunnar ^{[1
]}

Ahlberg, Elisabet ^{[2
]}

Karlsson, Maths ^{[3
]}

Matic, Aleksandar ^{[3
]}

Borjesson, Lars ^{[3
]}

机构：

[1] Chalmers, Dept Chem & Biol Engn, SE-41296 Gothenburg, Sweden

[2] Univ Gothenburg, Dept Chem, SE-41296 Gothenburg, Sweden

[3] Chalmers, Dept Appl Phys, SE-41296 Gothenburg, Sweden

来源：

JOURNAL OF THE ELECTROCHEMICAL SOCIETY | 2008年 / 155卷 / 11期

基金：

瑞典研究理事会;

关键词：

D O I：

10.1149/1.2969806

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

A wet chemical route has been used to synthesize the oxygen deficient perovskite BaZr0.5Yb0.5O3-delta. Analysis of X-ray powder diffraction data showed that both dried and hydrated samples adopt cubic crystal structures of space group Pm (3) over barm. Dynamic thermogravimetric analysis showed a significant mass loss for the hydrated sample compared to the dried sample, indicating that similar to 28% of the oxygen vacancies are filled by protonic defects. The strong O-H stretch band, 2500-3500 cm(-1), in the IR absorbance spectrum also clearly manifests the presence of significant levels of protons in the hydrated material. Proton conductivity was investigated on prehydrated (under dry Ar) and as-prepared (under wet Ar) samples. The heating cycle of the prehydrated sample showed higher proton conductivity compared to the cooling cycle, especially in the intermediate temperature range (150-550 degrees C). Finally, comparison with data for BaZr0.9Yb0.1O3-delta revealed that the more heavily doped sample showed higher proton conductivity compared to the more lightly doped sample. (C) 2008 The Electrochemical Society.

引用

页码：P97 / P102

页数：6

共 33 条

[1] Structural study and proton conductivity in Yb-doped BaZrO3 [J].

Ahmed, I. ;

Eriksson, S.-G. ;

Ahlberg, E. ;

Knee, C. S. ;

Gotlind, H. ;

Johansson, L.-G. ;

Karlsson, M. ;

Matic, A. ;

Borjesson, L. .

SOLID STATE IONICS, 2007, 178 (7-10) :515-520

[2] Proton conductivity and low temperature structure of In-doped BaZrO3 [J].

Ahmed, I. ;

Eriksson, S. -G. ;

Ahlberg, E. ;

Knee, C. S. ;

Karlsson, M. ;

Matic, A. ;

Engberg, D. ;

Borjesson, L. .

SOLID STATE IONICS, 2006, 177 (26-32) :2357-2362

[3] Synthesis and structural characterization of perovskite type proton conducting BaZr1-xInxO3-δ (0.0≤x≤0.75) [J].

Ahmed, I. ;

Eriksson, S-G. ;

Ahlberg, E. ;

Knee, C. S. ;

Berastegui, P. ;

Johansson, L-G. ;

Rundlof, H. ;

Karlsson, M. ;

Matic, A. ;

Borjesson, L. ;

Engberg, D. .

SOLID STATE IONICS, 2006, 177 (17-18) :1395-1403

[4] Influence of microstructure on electrical properties in BaZr0.5In0.5O3-δ proton conductor [J].

Ahmed, Istaq ;

Eriksson, Sten-G. ;

Ahlberg, Elisabet ;

Knee, Christopher S. .

SOLID STATE IONICS, 2008, 179 (21-26) :1155-1160

[5]

Bohn HG, 2000, J AM CERAM SOC, V83, P768

[6] TRANSPORT-PROPERTIES AND CONDUCTION MECHANISM IN HIGH-TEMPERATURE PROTONIC CONDUCTORS [J].

BONANOS, N .

SOLID STATE IONICS, 1992, 53 :967-974

[7] Investigations into Sr3CaZr0.5Ta1.5O8.75, a novel proton conducting perovskite oxide [J].

Corcoran, DJD ;

Irvine, JTS .

SOLID STATE IONICS, 2001, 145 (1-4) :307-313

[8] Indium doping in barium cerate: the relation between local symmetry and the formation and mobility of protonic defects [J].

Giannici, Francesco ;

Longo, Alessandro ;

Balerna, Antonella ;

Kreuer, Klaus-Dieter ;

Martorana, Antonino .

CHEMISTRY OF MATERIALS, 2007, 19 (23) :5714-5720

[9] Sinterability of commercial 8 mol% yttria-stabilized zirconia powders and the effect of sintered density on the ionic conductivity [J].

Gibson, IR ;

Dransfield, GP ;

Irvine, JTS .

JOURNAL OF MATERIALS SCIENCE, 1998, 33 (17) :4297-4305

[10] Protons and other defects in BaCeO3:: a computational study [J].

Glöckner, R ;

Islam, MS ;

Norby, T .

SOLID STATE IONICS, 1999, 122 (1-4) :145-156

← 1 2 3 4 →