Mechanical and thermal properties of nanocarbon-reinforced aluminum matrix composites at elevated temperatures

被引：130
作者：
Shin, S. E. [1 ]
Ko, Y. J. [1 ]
Bae, D. H. [1 ]
机构：
[1] Yonsei Univ, Dept Mat Sci & Engn, Seoul 03722, South Korea
来源：
COMPOSITES PART B-ENGINEERING | 2016年 / 106卷
基金：
新加坡国家研究基金会;
关键词：
Metal-matrix composites (MMCs); Mechanical properties; Thermal properties; Powder processing; CARBON NANOTUBES; AUTOMOTIVE APPLICATIONS; EXPANSION COEFFICIENTS; STRENGTHENING BEHAVIOR; RAMAN-SPECTRA; GRAPHENE; NANOCOMPOSITES; TRIBOLOGY; GRAPHITE; FRICTION;
D O I：
10.1016/j.compositesb.2016.09.017
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This study evaluated the mechanical and thermal properties of aluminum alloy 2024 (Al2024) matrix composites reinforced with multi-walled carbon nanotube (MWCNT) or few-layered graphene (FLG) in the temperature range of 250-430 degrees C. The Al2024/MWCNT and Al2024/FLG composites were fabricated using powder metallurgy, and the associated microstructures were observed. At 350 degrees C, both composites maintain high yield stress about 110 MPa, since uniform dispersion of the nano-scale reinforcements has a strong interface, hinders the dislocation movement and eutectic phase coarsening and severe softening of the matrix. The composites also show a low thermal expansion coefficient of similar to 18 x 10(-6)/K. The results are respectively over similar to 2.5 times higher strength and similar to 20% lower CTE than those of commercial Al alloy used as piston material (AlSi12CuMgNi). (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：66 / 73
页数：8
相关论文
共 46 条
  • [11] Thermal expansion behaviors of aluminum composite reinforced with carbon nanotubes
    Deng, C. F.
    Ma, Y. X.
    Zhang, P.
    Zhang, X. X.
    Wang, D. Z.
    [J]. MATERIALS LETTERS, 2008, 62 (16) : 2301 - 2303
  • [12] Alternative energy technologies
    Dresselhaus, MS
    Thomas, IL
    [J]. NATURE, 2001, 414 (6861) : 332 - 337
  • [13] Raman spectrum of graphene and graphene layers
    Ferrari, A. C.
    Meyer, J. C.
    Scardaci, V.
    Casiraghi, C.
    Lazzeri, M.
    Mauri, F.
    Piscanec, S.
    Jiang, D.
    Novoselov, K. S.
    Roth, S.
    Geim, A. K.
    [J]. PHYSICAL REVIEW LETTERS, 2006, 97 (18)
  • [14] Effects of composition and surface finish of silicon nitride tappet inserts on valvetrain friction
    Gangopadhyay, A
    McWatt, D
    Willermet, P
    Crosbie, GM
    Allor, RL
    [J]. LUBRICATION AT THE FRONTIER: THE ROLE OF THE INTERFACE AND SURFACE LAYERS IN THE THIN FILM AND BOUNDARY REGIME, 1999, 36 : 635 - 644
  • [15] Strengthening in carbon nanotube/aluminium (CNT/Al) composites
    George, R
    Kashyap, KT
    Raw, R
    Yamdagni, S
    [J]. SCRIPTA MATERIALIA, 2005, 53 (10) : 1159 - 1163
  • [16] Gmb HM, 2016, PISTONS ENGINE TESTI, VXIV, P296
  • [17] A VARIATIONAL APPROACH TO THE THEORY OF THE ELASTIC BEHAVIOUR OF MULTIPHASE MATERIALS
    HASHIN, Z
    SHTRIKMAN, S
    [J]. JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1963, 11 (02) : 127 - 140
  • [18] Thermal expansion of single wall carbon nanotubes
    Jiang, H
    Liu, B
    Huang, Y
    Hwang, KC
    [J]. JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 2004, 126 (03): : 265 - 270
  • [19] Raman spectra of graphite oxide and functionalized graphene sheets
    Kudin, Konstantin N.
    Ozbas, Bulent
    Schniepp, Hannes C.
    Prud'homme, Robert K.
    Aksay, Ilhan A.
    Car, Roberto
    [J]. NANO LETTERS, 2008, 8 (01) : 36 - 41
  • [20] Experimental and numerical study of alumina reinforced aluminum matrix composites: Processing, microstructural aspects and properties
    Kursun, Ali
    Bayraktar, Emin
    Enginsoy, Hal M.
    [J]. COMPOSITES PART B-ENGINEERING, 2016, 90 : 302 - 314
12345