C4A3S hydration in different alkaline media

被引：77
作者：
Sanchez-Herrero, M. J. [1 ]
Fernandez-Jimenez, A. [1 ]
Palomo, A. [1 ]
机构：
[1] CSIC, Eduardo Torroja Inst, Madrid 28033, Spain
来源：
CEMENT AND CONCRETE RESEARCH | 2013年 / 46卷
关键词：
Calorimetry; Hydration; pH; X-ray diffraction; Alkalis; FLY-ASH; CALCIUM; SYSTEM; ETTRINGITE; MECHANISM; SULFATE; CRYSTALLIZATION; 25-DEGREES-C; PERFORMANCE; OPC;
D O I：
10.1016/j.cemconres.2013.01.008
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
This study explored the behaviour of laboratory-synthesised calcium sulphoaluminate (C(4)A(3)S) in alkaline media. C(4)A(3)S was hydrated in three liquid media: water, 8-M NaOH and 4 (wt.%) Na2CO3 added to the C(4)A(3)S + water mix. Hydration kinetics were studied via isothermal conduction calorimetry and 2- and 28-day mechanical strength values were found. The reaction products were characterised with XRD and FTIR. The findings showed that whilst C(4)A(3)S hydration kinetics were accelerated in the presence of alkalis, the resulting pastes had lower mechanical strength than the pastes hydrated with water and exhibited severe decay in some cases. An analysis of the hydration products revealed the presence of ettringite in the water-hydrated C(4)A(3)S pastes, whereas under alkaline conditions the main calcium sulphoaluminate hydrate detected was U phase. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：41 / 49
页数：9
相关论文
共 58 条
[1]  
BARNHISEL R. I., 1965, SOIL SCI SOC AMER PROC, V29, P531
[2]   A porosimetric study of calcium sulfoaluminate cement pastes cured at early ages [J].
Bernardo, Graziella ;
Telesca, Antonio ;
Valenti, Gian Lorenzo .
CEMENT AND CONCRETE RESEARCH, 2006, 36 (06) :1042-1047
[3]   STRUCTURE OF CALCIUM ALUMINATE SULFATE CA4AL6O16S [J].
CALOS, NJ ;
KENNARD, CHL ;
WHITTAKER, AK ;
DAVIS, RL .
JOURNAL OF SOLID STATE CHEMISTRY, 1995, 119 (01) :1-7
[4]  
Chinchon Yepes S., 2008, MONOGRAFIA, P19
[5]  
Cohen M. D., 1980, 7 INT C CEM CHEM PAR, V4, P360
[6]   Calcium sulfoaluminate cement blended with OPC: A potential binder to encapsulate low-level radioactive slurries of complex chemistry [J].
Coumes, Celine Cau Dit ;
Courtois, Simone ;
Peysson, Sandrine ;
Ambroise, Jean ;
Pera, Jean .
CEMENT AND CONCRETE RESEARCH, 2009, 39 (09) :740-747
[7]   Effect of the Sio2/Na2O ratio on the alkali activation of fly ash.: Part II:: 29Si MAS-NMR Survey [J].
Criado, M. ;
Fernandez-Jimenez, A. ;
Palomo, A. ;
Sobrados, I. ;
Sanz, J. .
MICROPOROUS AND MESOPOROUS MATERIALS, 2008, 109 (1-3) :525-534
[8]   THERMODYNAMIC INVESTIGATION OF THE CAO-AL2O3-CACO3-H2O CLOSED-SYSTEM AT 25-DEGREES-C AND THE INFLUENCE OF NA2O [J].
DAMIDOT, D ;
STRONACH, S ;
KINDNESS, A ;
ATKINS, M ;
GLASSER, FP .
CEMENT AND CONCRETE RESEARCH, 1994, 24 (03) :563-572
[9]   THERMODYNAMIC INVESTIGATION OF THE CAO-AL2O3-CASO4-H2O SYSTEM AT 25-DEGREES-C AND THE INFLUENCE OF NA2O [J].
DAMIDOT, D ;
GLASSER, FP .
CEMENT AND CONCRETE RESEARCH, 1993, 23 (01) :221-238
[10]   Accuracy in Rietveld quantitative phase analysis of Portland cements [J].
De la Torre, AG ;
Aranda, MAG .
JOURNAL OF APPLIED CRYSTALLOGRAPHY, 2003, 36 :1169-1176
123456