A Comparative Study of Corrosion Behavior of Hard Anodized and Micro-Arc Oxidation Coatings on 7050 Aluminum Alloy

被引：35

作者：

Shao, Lianlian ^{[1
]}

Li, Hongtao ^{[1
,2
]}

Jiang, Bailing ^{[1
]}

Liu, Cancan ^{[1
]}

Gu, Xin ^{[1
]}

Chen, Dichun ^{[3
]}

机构：

[1] Nanjing Tech Univ, Coll Mat Sci & Engn, Nanjing 210009, Jiangsu, Peoples R China

[2] Univ Zaragoza, CSIC, Inst Ciencia Mat Aragon, E-50009 Zaragoza, Spain

[3] Xiamen Adv Mat Acad, Luoyang Ship Mat Res Inst, Xiamen 361006, Peoples R China

来源：

METALS | 2018年 / 8卷 / 03期

基金：

中国国家自然科学基金;

关键词：

micro-arc oxidation; hard anodization; microstructure; phase composition; corrosion behavior; SEALING TREATMENT; AL-ALLOY; MICROSTRUCTURE; RESISTANCE; ANODIZATION;

D O I：

10.3390/met8030165

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Two kinds of metal oxide coatings were fabricated on 7050 Al alloy by hard anodization (HA) and micro-arc oxidation (MAO) techniques. The microstructure, phase composition, and corrosion behavior of the two coatings were studied by scanning electron microscopy, X-ray diffraction, and corrosion tests, respectively. When compared with the HA coating, the MAO one was more effective to isolate the substrate from the corrosive environment. In addition, as confirmed by electrochemical tests, the MAO coating was of better corrosion resistance than the HA coating. Furthermore, it was revealed by neutral salt spray test that the MAO coating could protect substrate alloy over 1140 h, while the HA coating can only protect substrate alloy for 46 h due to the amorphous composition and through thickness defects (micro-pores and micro-cracks).

引用

页数：10

共 28 条

[11] Hard anodising of aerospace aluminium alloys [J].

Lerner, L. M. .

TRANSACTIONS OF THE INSTITUTE OF METAL FINISHING, 2010, 88 (01) :21-24

[12] Investigation of intrinsic mechanisms of aluminium anodization processes by analyzing the current density [J].

Li Yi ;

Ling Zhiyuan ;

Hu Xing ;

Liu Yisen ;

Chang Yi .

RSC ADVANCES, 2012, 2 (12) :5164-5171

[13] Electrochemical corrosion behaviors of a stress-aged Al-Zn-Mg-Cu alloy [J].

Lin, Y. C. ;

Zhang, Jin-Long ;

Chen, Ming-Song ;

Zhou, Ying ;

Ma, Xiang .

JOURNAL OF MATERIALS RESEARCH, 2016, 31 (16) :2493-2505

[14] Characterization and corrosion behavior of plasma electrolytic oxidation coated AZ91-T6 magnesium alloy [J].

Liu, Cancan ;

Liang, Jun ;

Zhou, Jiansong ;

Li, Qingbiao ;

Peng, Zhenjun ;

Wang, Lingqian .

SURFACE & COATINGS TECHNOLOGY, 2016, 304 :179-187

[15] Effect of the microstructure of Al 7050-T7451 on anodic oxide formation in sulfuric acid [J].

Liu, Jian-hua ;

Li, Ming ;

Li, Song-mei ;

Huang, Min .

INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2009, 16 (04) :432-438

[16] Formation and Corrosion Resistance of Micro-Arc Oxidation Coating on Equal-Channel Angular Pressed AZ91D Mg Alloy [J].

Ma, Aibin ;

Lu, Fumin ;

Zhou, Qi ;

Jiang, Jinghua ;

Song, Dan ;

Chen, Jianqing ;

Zheng, Yuxi .

METALS, 2016, 6 (12)

[17] Development of a theory for the determination of the composition of the anodizing solution inside the pores during the growth of porous anodic Al2O3 films on aluminium by a transport phenomenon analysis [J].

Patermarakis, G .

JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1998, 447 (1-2) :25-41

[18] Influence of dual-RRA temper on the exfoliation corrosion and electrochemical behavior of Al-Zn-Mg-Cu alloy [J].

Peng, G. -S. ;

Chen, K. -H. ;

Chen, S. -Y. ;

Fang, H. -C. .

MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2013, 64 (04) :284-289

[19] Role of grain-boundary precipitates and solute-depleted zone on the intergranular corrosion of aluminum alloy 7150 [J].

Ramgopal, T ;

Gouma, PI ;

Frankel, GS .

CORROSION, 2002, 58 (08) :687-697

[20] Model of structure of Al2O3 layer obtained via hard anodising method [J].

Skoneczny, W .

SURFACE ENGINEERING, 2001, 17 (05) :389-392

← 1 2 3 →