Influence of Ca2+ and Mg2+ as twinned ions on zirconia powder stability

Microstructure and the sintering behaviour of zirconia with twinned stabiliser ions: Ca2+ + Mg-2 in oxidative and in inert environment respectively obtained by solid state reactions method were studied. The specimens were cured at 1550 degrees C and 1750 degrees C in air in a kiln with methane gas. Samples with the same composition were sintered at 1550 degrees C in Argon in electrical furnace with (graphite electrodes). Their sinterability, microstructure as well as stability was studied The properties were compared as function of the processing route, the compositions stabilised in argon protective environment at 1550 degrees C or in air at 1750 degrees C, a totally stabilisation process was effective.