Secondary hardening and fracture behavior in alloy steels containing Mo, W, and Cr

In 4Mo, 6W, 2Mo3W, 2Mo2Cr, and 3W2Cr alloy steels, which contain alloying elements, such as Mo, W and Cr, contributing to the secondary hardening by forming M(2)C-type carbide, the secondary hardening and fracture behavior were studied. Molybdenum had a strong effect on secondary hardening, while W had a very weak effect on it but delayed the overaging. The MoW steel exhibited both moderately strong hardening and considerable resistance to overaging. On the other hand, the secondary hardening effect was diminished by the Cr addition, because the cementite of M(3)C type was stabilized at higher temperatures and the formation of M(2)C carbides was thus inhibited. Although the Cr addition had no merit in the secondary hardening itself, it eliminated the secondary hardening embrittlement (SHE). This was observed as a severe intergranular embrittlement due to the impurity segregation for the Mo and MoW steels and as a decrease in upper shelf energy for W steel, even in the overaged condition.