Effect of pre-strain and two-step aging on microstructure and stress corrosion cracking of 7050 alloy

被引：136

作者：

Wang, D. ^{[1
]}

Ni, D. R. ^{[1
]}

Ma, Z. Y. ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2008年 / 494卷 / 1-2期

关键词：

Aluminum; Stress corrosion cracking; Heat treatment; Pre-Strain; Grain boundary;

D O I：

10.1016/j.msea.2008.04.023

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A novel heat treatment procedure that combines the pre-strain with a two-step aging was proposed to improve both the strength and stress corrosion cracking (SCC) resistance of the high strength 7050 aluminum alloy. The heat treatment included a post-quenching pre-strain of 5%, a high-temperature aging at 200 degrees C for several minutes, and a subsequent low-temperature aging at 120 degrees C for 24h. The yield strength of the samples aged at 200 degrees C for 0.5 and 1 min was higher than that of the T6 sample. The SCC resistance of these samples was improved compared to the T6 sample, due to the enlargement in the size and the inter-particle distance of the grain boundaries precipitates and the decreases in the number of the GP zone. Especially, the sample aged at 200 degrees C for 5 min exhibited a similar SCC resistance and much higher elongation compared the T76 sample. (C) 2008 Elsevier B.V. All rights reserved.

引用

页码：360 / 366

页数：7

共 28 条

[1] EVIDENCE FOR DISLOCATION TRANSPORT OF HYDROGEN IN ALUMINUM [J].

ALBRECHT, J ;

BERNSTEIN, IM ;

THOMPSON, AW .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1982, 13 (05) :811-820

[2] GP-zones in Al-Zn-Mg alloys and their role in artificial aging [J].

Berg, LK ;

Gjonnes, J ;

Hansen, V ;

Li, XZ ;

Knutson-Wedel, M ;

Waterloo, G ;

Schryvers, D ;

Wallenberg, LR .

ACTA MATERIALIA, 2001, 49 (17) :3443-3451

[3] The effect of Cu on mechanical and precipitation properties of AI-Zn-Mg alloys [J].

Chinh, NQ ;

Lendvai, J ;

Ping, DH ;

Hono, K .

JOURNAL OF ALLOYS AND COMPOUNDS, 2004, 378 (1-2) :52-60

[4]

Cina B, 1974, Patent No. 3856584

[5]

Deschamps A, 1997, Z METALLKD, V88, P601

[6] Influence of predeformation on ageing in an Al-Zn-Mg alloy -: I.: Microstructure evolution and mechanical properties [J].

Deschamps, A ;

Livet, F ;

Bréchet, Y .

ACTA MATERIALIA, 1998, 47 (01) :281-292

[7] Structure-property correlations in Al 7050 and Al 7055 high-strength aluminum alloys [J].

Dixit, M. ;

Mishra, R. S. ;

Sankaran, K. K. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 478 (1-2) :163-172

[8] On the relationship between microstructure, strength and toughness in AA7050 aluminum alloy [J].

Dumont, D ;

Deschamps, A ;

Brechet, Y .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 356 (1-2) :326-336

[9] Characterization of precipitation microstructure and properties of 7150 aluminium alloy [J].

Fan, Xigang ;

Jiang, Daming ;

Meng, Qingchang ;

Lai, Zhonghong ;

Zhang, Xinmei .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 427 (1-2) :130-135

[10]

Hatch J.E., 1984, ALUMINUM PROPERTIES

← 1 2 3 →