Effect of Cr content and heat-treatment on the high temperature strength of eutectic Al-Si alloys

被引:82
作者
Yang, Yuying [1 ,2 ]
Zhong, Sheng-Yi [1 ]
Chen, Zhe [1 ]
Wang, Mingliang [2 ]
Ma, Naiheng [2 ]
Wang, Haowei [2 ]
机构
[1] Shanghai Jiao Tong Univ, State Key Lab Met Matrix Composites, Shanghai 200030, Peoples R China
[2] Shanghai Jiao Tong Univ, Sch Mat Sci & Engn, Shanghai 200240, Peoples R China
基金
中国国家自然科学基金;
关键词
Al-Si alloy; High temperature tensile strength; AlFeSi intermetallics; Heat treatment; FE-RICH INTERMETALLICS; CASTING ALLOYS; PISTON ALLOYS; MECHANICAL-PROPERTIES; FOUNDRY ALLOYS; IRON; MICROSTRUCTURE; NI; PHASES; EVOLUTION;
D O I
10.1016/j.jallcom.2015.05.167
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
In this work, the effects of Cr content (0-0.67 wt%) and heat treatment on the microstructure evolution and high temperature (HT) tensile strength (350 degrees C) of the Fe-containing eutectic Al-Si alloy were studied. The results show the main intermetallics are similar in tested specimens at both different heat treatment states, including gamma-Al3CuNi, delta-Al7Cu4Ni, Al4Cu2Mg8Si7, and AlFeSi. The addition of Cr leads to the transformation from needle-like beta-AlFeSi phases to fishbone-like alpha-Al(Fe, Cr) Si phases. For the HT strengths (350 degrees C), the UTSs of Al-Si alloys at T5 state are higher than T6 state correspondingly, both of which are progressively decreased with the Cr contents. For the elongation, the Al-Si alloys at T6 state have better plasticity than T5 state correspondingly. Comparably, the elongations remain stable at T5 state, and keep increasing at T6 state with the addition of Cr. The variations of HT strengths and elongations dependent on the Cr content and heat treatment are accounted on the microstructural evolutions, including AlFeSi phase transformation and the Si spheroidization. (C) 2015 Elsevier B.V. All rights reserved.
引用
收藏
页码:63 / 69
页数:7
相关论文
共 34 条
[1]   Three dimensional post-mortem study of damage after compression of cast Al-Si alloys [J].
Asghar, Z. ;
Requena, G. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 591 :136-143
[2]   The role of Ni and Fe aluminides on the elevated temperature strength of an AlSi12 alloy [J].
Asghar, Z. ;
Requena, G. ;
Kubel, F. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (21-22) :5691-5698
[3]   Three-dimensional study of Ni aluminides in an AlSi12 alloy by means of light optical and synchrotron microtomography [J].
Asghar, Z. ;
Requena, G. ;
Degischer, H. P. ;
Cloetens, P. .
ACTA MATERIALIA, 2009, 57 (14) :4125-4132
[4]   Thermal expansion of metals reinforced with ceramic particles and microcellular foams [J].
Balch, DK ;
Fitzgerald, TJ ;
Michaud, VJ ;
Mortensen, A ;
Shen, YL ;
Suresh, S .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (11) :3700-3717
[5]   INTERCONNEXION OF SILICON IN MODIFIED ALUMINIUM-SILICON EUTECTIC [J].
BELL, JAE ;
WINEGARD, WC .
NATURE, 1965, 208 (5006) :177-&
[6]   Constituent phase diagrams of the Al-Cu-Fe-Mg-Ni-Si system and their application to the analysis of aluminium piston alloys [J].
Belov, NA ;
Eskin, DG ;
Avxentieva, NN .
ACTA MATERIALIA, 2005, 53 (17) :4709-4722
[7]   Effect of Cr and Mn on the microstructure of spray-formed Al-25Si-5Fe-3Cu alloy [J].
Cai, Yuanhua ;
Liang, Ruiguang ;
Hou, Longgang ;
Zhang, Jishan .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (12) :4248-4254
[8]   The solidification characteristics of Fe-rich intermetallics in Al-11.5Si-0.4Mg cast alloys [J].
Cao, X ;
Campbell, J .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2004, 35A (05) :1425-1435
[9]   Investigation of mechanical properties of intermetallic phases in multi-component Al-Si alloys using hot-stage nanoindentation [J].
Chen, C. -L. ;
Richter, A. ;
Thomson, R. C. .
INTERMETALLICS, 2010, 18 (04) :499-508
[10]   Mechanical properties of intermetallic phases in multi-component Al-Si alloys using nanoindentation [J].
Chen, C. -L. ;
Richter, A. ;
Thomson, R. C. .
INTERMETALLICS, 2009, 17 (08) :634-641