Electrophoretic deposition of electroless nickel coated YSZ core-shell nanoparticles on a nickel based superalloy

In this work, yttria-stabilized zirconia (YSZ) nanoparticles were covered by a thin Ni layer with approximately 10 nm thickness by electroless deposition method to reduce sintering temperature of the ceramic coating which was applied on a Ni based superalloy via electrophoretic deposition (EPD). Suspensions containing the processed Ni-YSZ core -shell nanoparticles in acetone and isopropyl alcohol solvents were stabilized by addition of 0.4 wt% iodine and 1.5 wt% polyethylenimine, respectively, to find more effective stabilization method for EPD. It was seen that the presence of the Ni layer on YSZ nanoparticles improved performance and sticking factor of EPD and uniform coatings were obtained in both suspensions. The Ni-YSZ green coating which was produced by EPD at voltage of 35 V and deposition time of 30 min in acetone with thickness of 41 mu m was sintered in 1100 degrees C and finally a uniform NiO-YSZ coating was formed on the metallic surface.