Development of anisotropic microstructure in uniaxially pressed alumina compacts

被引:26
作者
Shui, AZ [1 ]
Saito, M [1 ]
Uchida, N [1 ]
Uematsu, K [1 ]
机构
[1] Nagaoka Univ Technol, Dept Chem, Nagaoka, Niigata 9402188, Japan
关键词
Al2O3; anisotropy; grain growth; pressing; sintering;
D O I
10.1016/S0955-2219(01)00434-4
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Alumina compacts are prepared by uniaxial pressing followed by cold isostatic pressing (CIP). Anisotropic micro structures of the compacts and their sintered bodies are reported. Anisotropic grain growth with sintering time was systematically examined through direct measurement of grain dimensions on SEM micrographs in various conditions. Experimental results indicated that average grain size was always larger in the plane parallel to the direction of uniaxial pressing, than in its perpendicular plane, for all sintering conditions. The difference in the average grain size increased in these planes with sintering time. The grain growth followed the cubic law and the rate constants were 4.8 x 10(-21) and 1.9 x 10(-21)(m(3)/s), for the former and the latter, respectively, in specimen uniaxial pressed at 100 MPa and CIPed at 100 MPa. Many intra-granule fractures were observed in the compact in the plane perpendicular the pressing direction comparing with its parallel plane. (C) 2002 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码:1217 / 1223
页数:7
相关论文
共 50 条
[31]   Microstructure and sintering of ceramic green compacts described in a constitutive model [J].
Shinagawa, K ;
Hirashima, Y ;
Kondo, Y .
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2000, 108 (01) :65-69
[32]   ANISOTROPIC GRAIN-GROWTH IN TIO2-DOPED ALUMINA [J].
HORN, DS ;
MESSING, GL .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1995, 195 (1-2) :169-178
[33]   Effect of internal binder on microstructure in compacts made from granules [J].
Tanaka, Satoshi ;
Chia-Pin, Chiu ;
Kato, Zenji ;
Uematsu, Keizo .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2007, 27 (2-3) :873-877
[34]   Microstructural evolution during sintering of near-monosized agglomerate-free submicron alumina powder compacts [J].
Lim, LC ;
Wong, PM ;
Jan, MA .
ACTA MATERIALIA, 2000, 48 (09) :2263-2275
[35]   Microstructure refinement of alumina Optimisation by gas pressure sintering process [J].
Nivot, C. ;
Valdivieso, F. .
CERAMICS INTERNATIONAL, 2008, 34 (07) :1595-1602
[36]   Effect of rapid heating on densification and grain growth in hot pressed alumina [J].
Murayama, N ;
Shin, W .
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2000, 108 (09) :799-802
[37]   Relationship between sintering shrinkage anisotropy and particle orientation for alumina powder compacts [J].
Shui, Anze ;
Zeng, Lingke ;
Uematsu, Keizo .
SCRIPTA MATERIALIA, 2006, 55 (09) :831-834
[38]   Anisotropic alumina ceramics with isotropic optical properties [J].
Ikesue, Akio ;
Aung, Yan Lin .
JOURNAL OF ADVANCED CERAMICS, 2023, 12 (01) :72-81
[39]   Anisotropic fracture in nacre-like alumina [J].
Duminy, Thomas ;
Henry, Ronan ;
Adrien, Jerome ;
Doitrand, Aurelien ;
Meille, Sylvain .
THEORETICAL AND APPLIED FRACTURE MECHANICS, 2023, 123
[40]   Remarkable anisotropic phonon response in uniaxially strained few-layer black phosphorus [J].
Yanlong Wang ;
Chunxiao Cong ;
Ruixiang Fei ;
Weihuang Yang ;
Yu Chen ;
Bingchen Cao ;
Li Yang ;
Ting Yu .
Nano Research, 2015, 8 :3944-3953