Preparation of a new water-based strippable protected coating

被引：3
|
作者：
Liu, Hongyu [1 ]
Zhang, Song [1 ]
机构：
[1] POB 7220, Beijing 100072, Peoples R China
来源：
ADVANCED MATERIALS, PTS 1-4 | 2011年 / 239-242卷
关键词：
water-based; strippable; coating; polyurethane; nano-CaCO3;
D O I：
10.4028/www.scientific.net/AMR.239-242.2646
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
A new water-based strippable protected coating was made by polyurethane emulsion and nano-CaCO3 was put in the coating as the fillers. The influence of nano-CaCO3 on the coating was discussed and the influence of film thickness on the coating was studied. The performance of the coating was tested, and when the dosage of nano-CaCO3 was 2% and the film thickness was 0.13 similar to 0.14mm, the film had the best strippable ability. Its average mechanics intensity was 5.72MPa and average elongation at break was 258.35%.
引用
收藏
页码：2646 / +
页数：2
相关论文
共 50 条
  • [21] Preparation of Water-based Nano-silver Gravure Conductive Ink Used for Printed Electronics
    Li Weiwei
    Mo Lixin
    Fu Jilan
    Li Wenbo
    Ran Jun
    Fan Xinming
    Li Yaling
    Li Luhai
    ADVANCES IN PRINTING AND PACKAGING TECHNOLOGIES, 2013, 262 : 523 - 526
  • [22] Effectiveness of a new water-based oil spill dispersant comprised of an alkyl polyglycoside
    Kim, JY
    Song, MG
    Kim, TS
    Kim, JD
    JOURNAL OF SURFACTANTS AND DETERGENTS, 1999, 2 (04) : 539 - 544
  • [23] Study on the Water Resistance of Polyurethane Water-Based Ink
    Fang Changqing
    Yu Ruien
    Zhou Shisheng
    Hu Jingbo
    Zhang Maorong
    Ren Penggang
    Wang Hongtao
    RESEARCH JOURNAL OF CHEMISTRY AND ENVIRONMENT, 2011, 15 (02): : 377 - 379
  • [24] A novel water-based cathode ink formulation
    Howe, Katie S.
    Clark, Ewan R.
    Bowen, James
    Kendall, Kevin
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2013, 38 (03) : 1731 - 1736
  • [25] A Tunable Water-based Metamaterial Microwave Absorber
    Han, Zixiang
    Zhao, Junming
    Feng, Yijun
    2017 IEEE SIXTH ASIA-PACIFIC CONFERENCE ON ANTENNAS AND PROPAGATION (APCAP), 2017,
  • [26] Porous YSZ ceramics by water-based gelcasting
    Gu, YF
    Liu, XQ
    Meng, GY
    Peng, DK
    CERAMICS INTERNATIONAL, 1999, 25 (08) : 705 - 709
  • [27] Chitosan as a water-based photoresist for DUV lithography
    Servin, Isabelle
    Teolis, Alexandre
    Bazin, Arnaud
    Sarrazin, Aurelien
    Durin, Paule
    Sysova, Olha
    Gablin, Corinne
    Saudet, Benoit
    Leonard, Didier
    Soppera, Olivier
    Leclercq, Jean-Louis
    Chevolot, Yann
    Tiron, Raluca
    Delair, Thierry
    Trombotto, Stephane
    ADVANCES IN PATTERNING MATERIALS AND PROCESSES XL, 2023, 12498
  • [28] Study on the gloss of polyurethane water-based ink
    Fang, C. Q.
    Zhou, S. S.
    Zhang, M. R.
    Ren, P. G.
    ADVANCES IN LIQUID CRYSTALS, 2010, 428-429 : 431 - 435
  • [29] The Modification of the Acrylate Emulsion for Water-Based Coatings
    Chen WeiFeng FaAi Zhang Key Laboratory of Nonferrous Materials and New Processing Technology Ministry of Education
    Department of Material and Chemical Engineering Guilin University of Technology Guilin China
    复旦学报(自然科学版), 2005, (05) : 289 - 290
  • [30] Preparation and properties of waterborne polyurethanes for water-vapor-permeable coating materials
    Kwak, YS
    Park, SW
    Lee, YH
    Kim, HD
    JOURNAL OF APPLIED POLYMER SCIENCE, 2003, 89 (01) : 123 - 129
12345