Preparation of a new water-based strippable protected coating

被引：3
|
作者：
Liu, Hongyu [1 ]
Zhang, Song [1 ]
机构：
[1] POB 7220, Beijing 100072, Peoples R China
来源：
ADVANCED MATERIALS, PTS 1-4 | 2011年 / 239-242卷
关键词：
water-based; strippable; coating; polyurethane; nano-CaCO3;
D O I：
10.4028/www.scientific.net/AMR.239-242.2646
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
A new water-based strippable protected coating was made by polyurethane emulsion and nano-CaCO3 was put in the coating as the fillers. The influence of nano-CaCO3 on the coating was discussed and the influence of film thickness on the coating was studied. The performance of the coating was tested, and when the dosage of nano-CaCO3 was 2% and the film thickness was 0.13 similar to 0.14mm, the film had the best strippable ability. Its average mechanics intensity was 5.72MPa and average elongation at break was 258.35%.
引用
收藏
页码：2646 / +
页数：2
相关论文
共 50 条
  • [1] Preparation of water-based anti-graffiti polyurethane coating
    Liu, Hu
    Zhu, Hongyan
    Shang, Qianqian
    Xiao, Guomin
    ADVANCES IN CHEMICAL, MATERIAL AND METALLURGICAL ENGINEERING, PTS 1-5, 2013, 634-638 : 2993 - 2996
  • [2] Preparation of a low contact angle water-based coating using ultrasonic irradiation
    Zhang, X. R.
    Liu, L. Z.
    Li, J. F.
    Cui, W. W.
    Weng, L.
    PIGMENT & RESIN TECHNOLOGY, 2014, 43 (06) : 341 - 346
  • [3] EFFECTS OF NANOCLAY CONTENTS ON THE PROPERTIES OF WATER-BASED COATING
    Anwar, U. M. K.
    Alia-Syahirah, Y.
    Tumirah, K.
    Hamdan, H.
    Lee, S. H.
    JOURNAL OF TROPICAL FOREST SCIENCE, 2019, 31 (03) : 353 - 361
  • [4] Water-based Anionic Polycarbodiimide Cross linker for coating
    Pang, Xiaoyan
    Ding, Zhiwen
    Jia, Jizhang
    Tong, Rong
    BIOTECHNOLOGY, CHEMICAL AND MATERIALS ENGINEERING, PTS 1-3, 2012, 393-395 : 1595 - +
  • [5] New water-based barrier coatings for paper and paperboard
    Vähä-Nissi, M
    Lahti, J
    Savolainen, A
    Rissa, K
    Lepistö, T
    APPITA JOURNAL, 2001, 54 (02): : 106 - 115
  • [6] Preparation and characterization of a water-based nanoparticle green polymer intended for application as a protective concrete coating against carbonation
    Nashed, Youssef L.
    Zahran, Fouad
    Youssef, Mohamed Adel
    EGYPTIAN JOURNAL OF CHEMISTRY, 2023, 66 (05): : 55 - 63
  • [7] Curing Properties of Water-based Self-drying/Fast-drying Foundry Coating
    Zhan, Chunyi
    Feng, Shengshan
    Xie, Shuzhong
    Liu, Chunjing
    Liang, Jiahao
    Gao, Yunhua
    PROCEEDINGS OF THE 3RD INTERNATIONAL CONFERENCE ON MATERIAL, MECHANICAL AND MANUFACTURING ENGINEERING, 2015, 27 : 1984 - 1989
  • [8] Effect of coating pigment type on paper printability with water-based inks
    Ozcan, Arif
    Sonmez, Sinan
    Tutak, Dogan
    JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, 2022, 19 (04) : 1149 - 1157
  • [9] Advances in the preparation of water-based inks based on chemical modification of rosin
    Zhang, Zhengquan
    Wang, Qiujing
    Zhang, Zhiming
    Li, Mingsheng
    He, Yunfei
    Shan, Shaoyun
    JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, 2025, 22 (02) : 511 - 525
  • [10] Durability and mechanical performance of a photo-catalytic water-based nanocomposite coating
    Khadem-Hosseini, A.
    Pazokifard, S.
    Mirabedini, S. M.
    PROGRESS IN ORGANIC COATINGS, 2017, 112 : 254 - 262
12345