Effects of Re content and crystallographic orientation on creep behavior of aluminized Ni-base single crystal superalloys

被引:29
作者
Latief, Fahamsyah H. [1 ]
Kakehi, Koji [1 ]
机构
[1] Tokyo Metropolitan Univ, Dept Mech Engn, Hachioji, Tokyo 1920397, Japan
关键词
Aluminide coating; Creep properties; Microstructure; Crystallographic orientation; MECHANICAL-PROPERTIES; MU-PHASE; MICROSTRUCTURE; INTERMEDIATE; ANISOTROPY; EVOLUTION;
D O I
10.1016/j.matdes.2013.01.022
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Effects of Re content and crystallographic orientation on creep behavior of aluminized Ni-base single crystal superalloys have been investigated in the present study. The addition of Re seemed to be effective for the creep strength improvement of Ni-base single crystal superalloys. The creep strength was significantly decreased in aluminized specimens due to the change in microstructure under coating layer by the formation of the interdiffusion zone (IDZ) and substrate diffusion zone (SDZ). The specimens with {1 0 0} side-surf ace showed longer creep rupture lives than the specimens with {1 10} side-surface which means that the anisotropic creep behavior took place. The anisotropic creep behavior was more evident in aluminized CM186LC than in aluminized PWA 1480. This anisotropic creep behavior was mainly induced by the discrepancy of fracture modes due to the different arrangement of slip systems, the geometry as well as the depth penetration of topologically close-packed (TCP) phases between the two side-surface orientations. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码:485 / 492
页数:8
相关论文
共 30 条
[1]   A comparative study of two inward grown Pt modified Al diffusion coatings on a single crystal Ni base superalloy [J].
Angenete, J ;
Stiller, K .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 316 (1-2) :182-194
[2]  
Biel M., 2001, MET FOUNDRY ENG, V27, P209
[3]   PHASE-COMPOSITION AND LONG-RANGE ORDER IN GAMMA'-PHASE OF A NICKEL-BASE SINGLE-CRYSTAL SUPERALLOY CMSX2 - AN ATOM PROBE STUDY [J].
BLAVETTE, D ;
BOSTEL, A .
ACTA METALLURGICA, 1984, 32 (05) :811-816
[4]   EFFECT OF ORIENTATION ON THE INTERMEDIATE TEMPERATURE CREEP-BEHAVIOR OF NI-BASE SINGLE-CRYSTAL SUPERALLOYS [J].
CARON, P ;
KHAN, T ;
NAKAGAWA, YG .
SCRIPTA METALLURGICA, 1986, 20 (04) :499-502
[5]  
Darolia R., 1988, SUPERALLOYS 1988, P255
[6]   Evolution of aluminide coating microstructure on nickel-base cast superalloy CM-247 in a single-step high-activity aluminizing process [J].
Das, DK ;
Singh, V ;
Joshi, SV .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (08) :2173-2188
[7]   Microstructural control of oxidation and corrosion resistant chromised nickel plated layers for Fe-Ni-Cr alloys [J].
Fujikawa, H ;
Makiura, H ;
Newcomb, SB .
MATERIALS SCIENCE AND TECHNOLOGY, 2002, 18 (11) :1347-1352
[8]   DEVELOPMENT OF 2 RHENIUM-CONTAINING SUPERALLOYS FOR SINGLE-CRYSTAL BLADE AND DIRECTIONALLY SOLIDIFIED VANE APPLICATIONS IN ADVANCED TURBINE-ENGINES [J].
HARRIS, K ;
ERICKSON, GL ;
SIKKENGA, SL ;
BRENTNALL, WD ;
AURRECOECHEA, JM ;
KUBARYCH, KG .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 1993, 2 (04) :481-488
[9]  
HARRIS K, 1986, HIGH TEMPERATURE ALL, P709
[10]   TCP suppression in a rutheniumm bearing single-crystal nickel-based superalloy [J].
Hobbs, R. A. ;
Zhang, L. ;
Rae, C. M. F. ;
Tin, S. .
JOM, 2008, 60 (07) :37-42