Precipitation Behavior of a Maraging Stainless Steel

被引：3
|
作者：
Jiang, Yue [1 ]
Ai, Ying Ying [1 ]
Wang, Qi Ting [1 ]
机构：
[1] Harbin Univ Sci & Technol, Coll Appl Sci, Harbin, Peoples R China
来源：
METALLURGY TECHNOLOGY AND MATERIALS | 2012年 / 567卷
关键词：
Maraging stainless steel; Thermodynamic calculation; Precipitation; Ageing treatment;
D O I：
10.4028/www.scientific.net/AMR.567.92
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The changes of precipitation phases and matrix structures in Fe-13Cr-7Ni-4Mo-4Co-2W maraging stainless steel at different temperature were studied by using the Thermo-Calc software. The research was on the microstructures and precipitation behaviors of the maraging stainless steel, the performance is investigated through solution and aging treatment by TEMand SADP. The calculation results were in good agreement with the experiments, which demonstrated that when maraging stainless steel was treated in high temperature, the Laves-Fe2Mo precipitates became totally dissolved as the temperature was above 1050 degrees C, and about 8% of R phase was found during aging. The calculation provides a guiding significant to the establishment of reasonable heat treatment process and the development of new materials.
引用
收藏
页码：92 / 95
页数：4
相关论文
共 50 条
  • [31] A STUDY OF PRECIPITATION IN STAINLESS AND MARAGING STEELS USING MOSSBAUER EFFECT
    MARCUS, H
    SCHWARTZ, LH
    FINE, ME
    ASM TRANSACTIONS QUARTERLY, 1966, 59 (03): : 468 - &
  • [32] Precipitation hardening in Monel K500, 17-4 PH stainless steel and 350 Grade Maraging Steel
    Viswanathan, UK
    Tewari, R
    Dey, GK
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2006, 59 (01): : 107 - 121
  • [33] STRENGTHENING AND TOUGHENING MECHANISMS OF MARAGING STAINLESS STEEL.
    Cao, Yang
    Chen, Fu-min
    Li, Guo-jun
    Yao, Jia-xin
    Gao, Hou-xiu
    Qin, Shi-qi
    Tianjin Daxue Xuebao (Ziran Kexue yu Gongcheng Jishu Ban)/Journal of Tianjin University Science and Technology, 1986, (02): : 27 - 37
  • [34] DELAYED FAILURE AND PRECIPITATION BEHAVIOR IN MARAGING STEELS
    ASAYAMA, Y
    TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1987, 28 (04): : 281 - 290
  • [35] Research on precipitates and relationship with martensite of maraging stainless steel
    Chen, Jia-Yan
    Liu, Jiang
    Yang, Zhuo-Yue
    Zhang, Yong-Quan
    Kang T'ieh/Iron and Steel (Peking), 2008, 43 (03): : 81 - 85
  • [36] PRECIPITATION BEHAVIOR OF AUSTENITE IN AGED MARAGING STEELS
    OKADA, Y
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 : 1551 - 1551
  • [37] Electron Beam Welding of Dissimilar Stainless Steel and Maraging Steel Joints
    Gel'atko, Matus
    Vandzura, Radoslav
    Botko, Frantisek
    Hatala, Michal
    MATERIALS, 2024, 17 (23)
  • [38] Microstructure evolution and corrosion behavior of the novel maraging stainless steel manufactured by selective laser melting
    Lu, Zhen
    Zhang, Chengcai
    Fang, Ruirui
    Zhang, Hongbin
    Zhou, Haiping
    Deng, Nana
    Guo, Zhenzhen
    Gu, Lianwang
    MATERIALS CHARACTERIZATION, 2022, 190
  • [39] Peculiarities of deformation behavior of magnetic parameters of a maraging steel characterized by different degrees of precipitation hardening
    E. S. Gorkunov
    S. Yu. Mitropol’skaya
    S. M. Zadvorkin
    A. L. Osintseva
    D. I. Vichuzhanin
    Russian Journal of Nondestructive Testing, 2007, 43 : 567 - 575
  • [40] The influence of retained austenite on precipitation hardening of maraging steel
    Kladaric, I.
    Krumes, D.
    Vitez, I.
    METALURGIJA, 2007, 46 (02): : 97 - 99
12345