Analysis of aluminum sheets with multiple sites damage based on fatigue tests and DIC technique

被引：24

作者：

Chen, Yajun ^{[1
]}

Sun, Shengjie ^{[1
]}

Ji, Chunming ^{[1
]}

机构：

[1] Civil Aviat Univ China, Sinoeuropean Inst Aviat Engn, Tianjin 300300, Peoples R China

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2018年 / 109卷

基金：

中国国家自然科学基金;

关键词：

Multiple sites damage; Digital image correlation; Non-collinear crack; Fatigue; DIGITAL IMAGE CORRELATION; THERMOMECHANICAL RESPONSE; CRACK DEFLECTION; STAGE-II; LIFE; MECHANISMS; GROWTH; METHODOLOGY;

D O I：

10.1016/j.ijfatigue.2017.12.008

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

In order to study the multiple sites damage (MSD) under fatigue loading which was occurring in the airframe of aging aircraft, the digital image correlation (DIC) technique was used to evaluate MSD in the hollow pre-notched specimen with 2024-T4 aluminum alloy subjected to cyclic loading conditions. Fatigue lives and displacement fields obtained from digital images recorded during fatigue tests were used to analyze the crack initiation and propagation. The results show that the fatigue life increases with the increase of hole spacing and that the case of collinear cracks becomes more dangerous than that of non-collinear cracks for MSD specimens. The experiments and DIC analyses were carried out to validate the type of fatigue crack propagation, firstly by mode I, and then by the mode I and II with hybrid expansion. Based on the combination of ABAQUS and Paris formula, stress intensity factors (SIF) and fatigue lives were acquired, which provide the conservative estimation of fatigue life.

引用

页码：37 / 48

页数：12

共 43 条

[1]

Bakuckas Jr JG, 2007, P 24 ICAF S DUR DAM, P749

[2] Crack opening displacement for two unequal straight cracks with coalesced plastic zones - A modified Dugdale model [J].

Bhargava, R. R. ;

Hasan, S. .

APPLIED MATHEMATICAL MODELLING, 2011, 35 (08) :3788-3796

[3] Characterization of the deformation behaviors associated with the serrated flow of a 5456 Al-based alloy using two orthogonal digital image correlation systems [J].

Cai, Y. L. ;

Yang, S. L. ;

Wang, Y. H. ;

Fu, S. H. ;

Zhang, Q. C. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 664 :155-164

[4] A Technique for Coupled Thermomechanical Response Measurement Using Infrared Thermography and Digital Image Correlation (TDIC) [J].

Cholewa, N. ;

Summers, P. T. ;

Feih, S. ;

Mouritz, A. P. ;

Lattimer, B. Y. ;

Case, S. W. .

EXPERIMENTAL MECHANICS, 2016, 56 (02) :145-164

[5]

Corten H.T., 1956, International Conference on Fatigue of Metals, Institution of Mechanical Engineering and American Society of Mechanical Engineers, P235

[6] CTOA AND CRACK-TUNNELING MEASUREMENTS IN THIN SHEET 2024-T3 ALUMINUM-ALLOY [J].

DAWICKE, DS ;

SUTTON, MA .

EXPERIMENTAL MECHANICS, 1994, 34 (04) :357-368

[7] An experimental study on crack propagation at rock-concrete interface using digital image correlation technique [J].

Dong, Wei ;

Wu, Zhimin ;

Zhou, Xiangming ;

Wang, Na ;

Kastiukas, Gediminas .

ENGINEERING FRACTURE MECHANICS, 2017, 171 :50-63

[8] Analysis of anisotropic damage in forged Al-Cu-Mg-Si alloy based on creep tests, micrographs of fractured specimen and digital image correlations [J].

Gariboldi, Elisabetta ;

Naumenko, Konstantin ;

Ozhoga-Maslovskaja, Oksana ;

Zappa, Emanuele .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 652 :175-185

[9]

Gasson P.C., 2014, AERONAUT J, V118, P979, DOI [10.1017/S0001924000009672, DOI 10.1017/S0001924000009672]

[10] A FINITE-ELEMENT ANALYSIS OF MIXED-MODE FRACTURE INITIATION BY DUCTILE FAILURE MECHANISMS [J].

GHOSAL, AK ;

NARASIMHAN, R .

JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1994, 42 (06) :953-978

← 1 2 3 4 5 →