Softening and Melting Behavior of Mixed Burden for Oxygen Blast Furnace

被引：46

作者：

An Xiu-wei ^{[1
]}

Wang Jing-song ^{[1
]}

Lan Rong-zong ^{[1
]}

Han Yi-hua ^{[1
]}

Xue Qing-guo ^{[1
]}

机构：

[1] Univ Sci & Technol Beijing, Sch Met & Ecol Engn, State Key Lab Adv Met, Beijing 100083, Peoples R China

来源：

JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL | 2013年 / 20卷 / 05期

关键词：

oxygen blast furnace; softening; melting; mixed burden; basicity; reduction degree;

D O I：

10.1016/S1006-706X(13)60090-4

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The behaviors of mixed burden in the cohesive zone of oxygen blast furnace were studied by softening and melting tests, and the influence of reducing gas and burden basicity on the softening and melting behaviors of mixed burden was also investigated. The results indicated that the softening range became wide, however, the melting range narrowed sharply in the atmosphere of oxygen blast furnace. The permeability of burden in the oxygen blast furnace was obviously improved comparing with the conventional blast furnace. In addition, the content of sulphur in the dripping iron of oxygen blast furnace was much lower than that of conventional blast furnace, however, the content of carbon increased. An optimum basicity of burden, which could lead to the appearance of the narrower melting range and better permeability of burden, was obtained in the atmosphere of oxygen blast furnace.

引用

页码：11 / 16

页数：6

共 18 条

[1]

[Anonymous], MIXED BURDEN SOFTENI

[2] Prediction of blast furnace performance with top gas recycling [J].

Austin, PR ;

Nogami, H ;

Yagi, J .

ISIJ INTERNATIONAL, 1998, 38 (03) :239-245

[3]

Bakker T, 1999, SOFTENING BLAST FURN

[4] ULCOS - Pilot testing of the Low-CO2 Blast Furnace process at the experimental BF in Lulea [J].

Danloy, G. ;

Berthelemot, A. ;

Grant, M. ;

Borlee, J. ;

Sert, D. ;

van der Stel, J. ;

Jak, H. ;

Dimastromatteo, V. ;

Hallin, M. ;

Eklund, N. ;

Edberg, N. ;

Sundqvist, L. ;

Skoeld, B. -E. ;

Lin, R. ;

Feiterna, A. ;

Korthas, B. ;

Mueller, F. ;

Feilmayr, C. ;

Habermann, A. .

REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 2009, 106 (01) :1-+

[5]

Fink F., 1996, STEEL TIMES UK, V224, P398

[6]

[韩毅华 Han Yihua], 2011, [北京科技大学学报, Journal of University Science and Technology Beijing], V33, P1280

[7]

Lu W.K., 1984, ISS T, V5, P25

[8]

Nogueira P F, 2003, BLAST FURNACE BURDEN

[9] PROCESS CHARACTERISTICS OF A COMMERCIAL-SCALE OXYGEN BLAST-FURNACE PROCESS WITH SHAFT GAS INJECTION [J].

OHNO, Y ;

MATSUURA, M ;

MITSUFUJI, H ;

FURUKAWA, T .

ISIJ INTERNATIONAL, 1992, 32 (07) :838-847

[10]

Okamoto T, 1972, TETSU TO HAGANE, V58, P637

← 1 2 →