Effects of heat treatment and addition of small amounts of Cu and Mg on the microstructure and mechanical properties of Al-Si-Cu and Al-Si-Mg cast alloys

被引:98
作者
Beroual, Said [1 ]
Boumerzoug, Zakaria [1 ]
Paillard, Pascal [2 ]
Borjon-Piron, Yann [2 ]
机构
[1] Univ Biskra, Dept Mech Engn, LMSM, BP 145, Biskra 07000, Algeria
[2] Inst Mat Jean Rouxel, IMN ID2M, UMR 6502, BP 50609, F-44306 Nantes, France
关键词
Al-Si-Cu; Al-Si-Mg; Intermetallic; Solution heat treatment; Aging; Precipitation; COOLING RATE; SOLIDIFICATION CHARACTERISTICS; INTERMETALLIC COMPOUNDS; AS-CAST; FE; IRON; BEHAVIOR; A356; MANGANESE; DUCTILITY;
D O I
10.1016/j.jallcom.2018.12.365
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The present study investigates the effects of heat treatment on the microstructures and mechanical properties of Al-Si-Cu and Al-Si-Mg alloys containing small amounts of added copper and magnesium, with the aim of obtaining the maximum alloy hardness via the adjustment of the solution heat treatment and aging. The solution heat treatment was performed at 500 degrees C and 525 degrees C for the Al-Si-Cu alloy and at 525 degrees C for the Al-Si-Mg alloy. The samples of both alloys were solution treated for various times between 5 min and 16 h, followed by quenching and finally an artificial aging was performed at 210 degrees C for a time ranging from 10 min to 50 h. The microstructures of the as-cast alloys and heat-treated samples were studied using optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction and hardness tests. The results show that the solution treatment time significantly affects the coarseness of the microstructure, causes the dissolution of the intermetallic phases, and homogenizes the distribution of copper and magnesium in the matrix. The peak-aged Al-Si-Cu alloy was obtained after a solution heat treatment at 525 degrees C for 15 min followed by 2 h of aging. The peak-aged Al-Si-Mg alloy was obtained after 8 h of solution heat treatment at 525 degrees C followed by 40 min of aging. The Al-SiMg alloy with the 0.6 wt% Mg addition displayed an age-hardening response that was approximately 34% higher than that of the Al-Si-Cu alloy with a 0.3 wt% Cu addition. (C) 2018 Published by Elsevier B.V.
引用
收藏
页码:1026 / 1035
页数:10
相关论文
共 36 条
[1]   Effect of cooling rate and Mg content on the Al-Si eutectic for Al-Si-Cu-Mg alloys [J].
Aguilera-Luna, I. ;
Castro-Roman, M. J. ;
Escobedo-Bocardo, J. C. ;
Garcia-Pastor, F. A. ;
Herrera-Trejo, M. .
MATERIALS CHARACTERIZATION, 2014, 95 :211-218
[2]   Aging behavior of 359-type Al-9% Si-0.5% Mg casting alloys [J].
Ammar, H. R. ;
Samuel, A. M. ;
Samuel, F. H. ;
Al-Ahmari, A. M. A. .
JOURNAL OF MATERIALS SCIENCE, 2012, 47 (03) :1331-1338
[3]  
[Anonymous], 1943, METALLOGRAPHY ALUMIN
[4]   Effect of cooling rate and Fe/Mn weight ratio on volume fractions of α-AlFeSi and β-AlFeSi phases in Al-7.3Si-3.5Cu alloy [J].
Belmares-Perales, S. ;
Castro-Roman, M. ;
Herrera-Trejo, M. ;
Ramirez-Vidaurri, L. E. .
METALS AND MATERIALS INTERNATIONAL, 2008, 14 (03) :307-314
[5]   Refinement of the grain size of the LM25 alloy (A356) by 96Al-2Nb-2B master alloy [J].
Bolzoni, L. ;
Babu, N. Hari .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2015, 222 :219-223
[6]   Enhanced ductility in Al-Si-Cu-Mg foundry alloys with high Si content [J].
Caceres, C. H. ;
Taylor, J. A. .
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2006, 37 (06) :897-903
[7]   Strength-ductility behaviour of Al-Si-Cu-Mg casting alloys in T6 temper [J].
Cáceres, CH ;
Svensson, IL ;
Taylor, JA .
INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2003, 15 (05) :531-543
[8]   The solidification characteristics of Fe-rich intermetallics in Al-11.5Si-0.4Mg cast alloys [J].
Cao, X ;
Campbell, J .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2004, 35A (05) :1425-1435
[9]   Effect of iron and manganese contents on convection-free precipitation and sedimentation of primary α-Al(FeMn)Si phase in liquid Al-11.5Si-0.4Mg alloy [J].
Cao, X ;
Saunders, N ;
Campbell, J .
JOURNAL OF MATERIALS SCIENCE, 2004, 39 (07) :2303-2314
[10]   CRYSTAL STRUCTURE OF TERNARY ALLOY ALPHA(ALFESI) [J].
COOPER, M .
ACTA CRYSTALLOGRAPHICA, 1967, 23 :1106-&