Static and fatigue failure analysis of adhesively bonded thick composite single lap joints

被引：62

作者：

Tang, J. H. ^{[1
]}

Sridhar, I. ^{[1
,2
]}

Srikanth, N. ^{[2
]}

机构：

[1] Nanyang Technol Univ, Sch Mech & Aerosp Engn, Singapore 639798, Singapore

[2] Nanyang Technol Univ, Energy Res Inst, Singapore 637141, Singapore

来源：

COMPOSITES SCIENCE AND TECHNOLOGY | 2013年 / 86卷

关键词：

Adhesive joints; Fatigue; Interface; Finite element analysis; STRESS SINGULARITY APPROACH; BONDLINE THICKNESS; STRUCTURAL ADHESIVES; INTENSITY FACTORS; FRACTURE; BEHAVIOR; PREDICTION; INITIATION; CRITERION; STRENGTH;

D O I：

10.1016/j.compscitech.2013.06.018

中图分类号：

TB33 [复合材料];

学科分类号：

摘要：

Static and fatigue behavior of thick composite laminate single lap joints with thick adhesive bondline is experimentally and numerically investigated. Stress based analysis is used to understand the uniaxial tensile behavior of thick glass fiber reinforced epoxy laminates bonded with relatively thick epoxy adhesive. The effect of adhesive thickness on relatively thick adherend on the fatigue initiation life was modeled with generalized stress singularity approach. It was observed that the failure onset always occurred at adherend-adhesive interface. Subsequent crack propagation mostly resulted in interlaminar failure of adjacent first angle ply near to this interface. Both static and fatigue strength values decrease with increase of bondline thickness. Evaluation of generalized stress intensity factors of the corner geometry (square edge joint) provided a good correlation between predictions and experimental measurements. (C) 2013 Elsevier Ltd. All rights reserved.

引用

页码：18 / 25

页数：8

共 39 条

[11] Composite adhesive joints under cyclic loading [J].

de Goeij, WC ;

van Tooren, MJL ;

Beukers, A .

MATERIALS & DESIGN, 1999, 20 (05) :213-221

[12] A stress singularity approach to failure initiation in a bonded joint with varying bondline thickness [J].

Gleich, DM ;

Van Tooren, MJL ;

Beukers, A .

JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2001, 15 (10) :1247-1259

[13] Analysis and evaluation of bondline thickness effects on failure load in adhesively bonded structures [J].

Gleich, DM ;

Van Tooren, MJL ;

Beukers, A .

JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2001, 15 (09) :1091-1101

[14]

Goland M., 1944, J. Appl. Mech, V11, P1727, DOI [10.1007/BF00534409, DOI 10.1007/BF00534409]

[15] A FRACTURE CRITERION FOR EDGE-BONDED BIMATERIAL BODIES [J].

GRADIN, PA .

JOURNAL OF COMPOSITE MATERIALS, 1982, 16 (NOV) :448-456

[16]

Groth H.L., 1985, International Journal of Adhesion and Adhesives, V5, P19

[17] STRESS SINGULARITIES AND FRACTURE AT INTERFACE CORNERS IN BONDED JOINTS [J].

GROTH, HL .

INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 1988, 8 (02) :107-113

[18] FATIGUE LIFE EVALUATION OF STRUCTURAL ADHESIVES FOR AUTOMOTIVE APPLICATIONS [J].

HARRIS, JA ;

FAY, PA .

INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 1992, 12 (01) :9-18

[19]

Hart-Smith LJ, 2002, J COMPOS TECH RES, V24, P133

[20] Evaluation of fatigue life of adhesively bonded aluminum single-lap joints using interfacial parameters [J].

Jen, Yi-Ming ;

Ko, Chih-Wei .

INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (02) :330-340

← 1 2 3 4 →