Static and fatigue failure analysis of adhesively bonded thick composite single lap joints

被引：62

作者：

Tang, J. H. ^{[1
]}

Sridhar, I. ^{[1
,2
]}

Srikanth, N. ^{[2
]}

机构：

[1] Nanyang Technol Univ, Sch Mech & Aerosp Engn, Singapore 639798, Singapore

[2] Nanyang Technol Univ, Energy Res Inst, Singapore 637141, Singapore

来源：

COMPOSITES SCIENCE AND TECHNOLOGY | 2013年 / 86卷

关键词：

Adhesive joints; Fatigue; Interface; Finite element analysis; STRESS SINGULARITY APPROACH; BONDLINE THICKNESS; STRUCTURAL ADHESIVES; INTENSITY FACTORS; FRACTURE; BEHAVIOR; PREDICTION; INITIATION; CRITERION; STRENGTH;

D O I：

10.1016/j.compscitech.2013.06.018

中图分类号：

TB33 [复合材料];

学科分类号：

摘要：

Static and fatigue behavior of thick composite laminate single lap joints with thick adhesive bondline is experimentally and numerically investigated. Stress based analysis is used to understand the uniaxial tensile behavior of thick glass fiber reinforced epoxy laminates bonded with relatively thick epoxy adhesive. The effect of adhesive thickness on relatively thick adherend on the fatigue initiation life was modeled with generalized stress singularity approach. It was observed that the failure onset always occurred at adherend-adhesive interface. Subsequent crack propagation mostly resulted in interlaminar failure of adjacent first angle ply near to this interface. Both static and fatigue strength values decrease with increase of bondline thickness. Evaluation of generalized stress intensity factors of the corner geometry (square edge joint) provided a good correlation between predictions and experimental measurements. (C) 2013 Elsevier Ltd. All rights reserved.

引用

页码：18 / 25

页数：8

共 39 条

[1]

Adams R.D., 1974, J STRAIN ANAL, V9, P185, DOI [10.1243/03093247V093185, DOI 10.1243/03093247V093185]

[2] On the singular stress field near the edge of bonded joints [J].

Akisanya, AR .

JOURNAL OF STRAIN ANALYSIS FOR ENGINEERING DESIGN, 1997, 32 (04) :301-311

[3] THEORY FOR ELASTIC STRESSES IN ADHESIVE BONDED LAP JOINTS [J].

ALLMAN, DJ .

QUARTERLY JOURNAL OF MECHANICS AND APPLIED MATHEMATICS, 1977, 30 (NOV) :415-436

[4] Static and fatigue behaviour of room temperature vulcanising silicone adhesives for high temperature aerospace applications [J].

Banea, M. D. ;

da Silva, L. F. M. .

MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2010, 41 (05) :325-335

[5] Singularity analysis of anisotropic multimaterial corners [J].

Barroso, A ;

Mantic, V ;

París, F .

INTERNATIONAL JOURNAL OF FRACTURE, 2003, 119 (01) :1-23

[6] A PATH INDEPENDENT INTEGRAL FOR COMPUTING STRESS INTENSITIES FOR V-NOTCHED CRACKS IN A BI-MATERIAL [J].

CARPENTER, WC ;

BYERS, C .

INTERNATIONAL JOURNAL OF FRACTURE, 1987, 35 (04) :245-268

[7] Effect of Bondline Thickness on the Static Strength of Structural Adhesives Under Nearly-Homogeneous Shear Stresses [J].

Castagnetti, D. ;

Spaggiari, A. ;

Dragoni, E. .

JOURNAL OF ADHESION, 2011, 87 (7-8) :780-803

[8] AN ANALYSIS OF ADHESIVE-BONDED SINGLE-LAP JOINTS [J].

CHEN, D ;

CHENG, S .

JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 1983, 50 (01) :109-115

[9] GLOBAL YIELDING AS A FAILURE CRITERION FOR BONDED JOINTS [J].

CROCOMBE, AD .

INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 1989, 9 (03) :145-153

[10] Effect of adhesive type and thickness on the lap shear strength [J].

da Silva, Lucas F. M. ;

Rodrigues, T. N. S. S. ;

Figueiredo, M. A. V. ;

de Moura, M. F. S. F. ;

Chousal, J. A. G. .

JOURNAL OF ADHESION, 2006, 82 (11) :1091-1115

← 1 2 3 4 →