TYPE IV CREEP RUPTURE CHARACTERISTICS OF P92 STEEL WELDMENT

被引:7
|
作者
Wang Xue [1 ]
Pan Qiangang [2 ]
Tao Yongshun [2 ]
Zhang Yinglin [1 ]
Zeng Huiqiang [2 ]
Liu Hong [2 ]
机构
[1] Wuhan Univ, Sch Power & Mech, Wuhan 430072, Peoples R China
[2] Dongfang Boiler Grp Co Ltd, Dongfang Elect Corp, Zigong 643001, Peoples R China
基金
中国国家自然科学基金;
关键词
ultra-supercritical unit; 1392; steel; creep; type IV cracking; microstucture; void; HEAT-RESISTANT STEELS; HIGH CR STEEL; HIGH-TEMPERATURE; PARTICLE-SIZE; WELDED-JOINTS; LAVES PHASE; STRENGTH; BEHAVIOR; FRACTURE; HAZ;
D O I
10.3724/SP.J.1037.2011.00646
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Creep tests at 600-650 degrees C with applied stresses in the range 100-240 MPa and microstructural observations by means of OM, SEM, TEM were conducted on welded joints of P92 steel prepared by submerged arc welding (SAW) process to investigated its characteristics of type IV creep rupture. The results showed that type IV failure tack place at higher temperature and lower stress and tends to have a critical condition expressed by Larson-Miller parameter (LMP) and stress level which values are 35.5 and 120 MPa, respectively. Type IV failure showed a lack of ductility and located in the fine grained heat affected zone (FGHAZ) (heated to just above A(C3))close to intercritical heat affected zone (HAZ), where microstructural changes are obviously different from those in the base metal, including formation of equiaxed sub-grain structure, mass precipitation and rapid growth of Laves phases on the grain boundaries during creep exposure, which lead to the type IV failure. The size of M23C6 carbide in the FGHAZ was almost the same as that in the base metal, which has little effect on the failure. Type IV rupture is a brittle intergranular fracture due to cavity coalescence, which was nucleated at coarse precipitates of Laves phase. The fraction of grain boundary facets cavitated and the area fraction of voids can be employed to quantify grain boundary damage and evaluate type IV failure of P92 steel welded joints, and when their values were about 1.2% and 0.5%, type IV failure would occur.
引用
收藏
页码:427 / 434
页数:8
相关论文
共 28 条
  • [1] Microstructural instability of a welded joint in P91 steel during creep at 600°C
    Abd El-Azim, ME
    Nasreldin, AM
    Zies, G
    Klenk, A
    [J]. MATERIALS SCIENCE AND TECHNOLOGY, 2005, 21 (07) : 779 - 790
  • [2] Variation in the Type IV cracking behaviour of a high Cr steel weld with post weld heat treatment
    Albert, SK
    Matsui, M
    Watanabe, T
    Hongo, H
    Kubo, K
    Tabuchi, M
    [J]. INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2003, 80 (06) : 405 - 413
  • [3] Chen BL, 2006, IMPERFECTION ANAL CO, P301
  • [4] Quantification of the Laves phase in advanced 9-12% Cr steels using a standard SEM
    Dimmler, G
    Weinert, P
    Kozeschnik, E
    Cerjak, H
    [J]. MATERIALS CHARACTERIZATION, 2003, 51 (05) : 341 - 352
  • [5] High temperature creep flow and damage properties of 9Cr1MoNbV steels: Base metal and weldment
    Gaffard, V
    Gourgues-Lorenzon, AF
    Besson, J
    [J]. NUCLEAR ENGINEERING AND DESIGN, 2005, 235 (24) : 2547 - 2562
  • [6] Precipitate stability in creep resistant ferritic steels - Experimental investigations and modelling
    Hald, J
    Korcakova, L
    [J]. ISIJ INTERNATIONAL, 2003, 43 (03) : 420 - 427
  • [7] Evaluation of particle size distributions of precipitates in a 9% chromium steel using energy filtered transmission electron microscopy
    Hättestrand, M
    Andrén, HO
    [J]. MICRON, 2001, 32 (08) : 789 - 797
  • [8] Holdsworth S.R., 2005, ECCC DATA SHEETS 200, P47
  • [9] Jorgen B., 2006, ENERGY, V31, P1437
  • [10] HAZ SOFTENING AND CREEP-RUPTURE STRENGTH OF HIGH CR FERRITIC STEEL WELDMENTS
    KOJIMA, T
    HAYASHI, K
    KAJITA, Y
    [J]. ISIJ INTERNATIONAL, 1995, 35 (10) : 1284 - 1290