Superplastic forming of corrosion resistance CuZnSn alloys

被引：3
作者：
Matsubara, R
Ashie, N
Nakamura, K
Miura, S
机构：
[1] TOTO Ltd, R&D Ctr, Kokura R&D Div, Kokurakita Ku, Kitakyushu, Fukuoka 8028601, Japan
[2] Kumamoto Inst Technol, Fac Engn, Dept Mech Engn, Kumamoto 8600082, Japan
来源：
TOWARDS INNOVATION IN SUPERPLASTICITY II | 1999年 / 304-3卷
关键词：
grain refinement; ratio of alpha/beta; interphase interfaces sliding;
D O I：
10.4028/www.scientific.net/MSF.304-306.753
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The new commercial Cu-Zn based alloys having excellent hot workability and corrosion resistance were developed. Higher than 200% elongation was observed in the hot tensile test with the alloy sample containing Cu-37.9Zn-1.87Sn-1.91wt%Pb at the temperature range from 500 to 600 degrees C at the initial strain rate of 8.3x10(-4) s(-1). The stress-strain curve showed the typical type of superplastic deformation. The alloy samples were made by the usual method to produce commercial brass. In order to refine the grain size, the temperature of hot extrusion was taken from 530 to 580 degrees C which is lower than the temperature above 700 degrees C generally used. Also the certain ratio of alpha / beta phase was adjusted to increase the sliding between alpha and beta interphase interfaces. The grain size refinement and the ratio of alpha / beta phase adjustment increase the elongation at hot workability range.
引用
收藏
页码：753 / 758
页数：6
相关论文
共 50 条
[21]   Improvement of formability and corrosion resistance of AZ31 magnesium alloy by pulsed current-assisted laser shock forming [J].
Liu, Huixia ;
Sun, Yuhao ;
Ma, Youjuan ;
He, Yanchen ;
Wang, Xiao .
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2022, 120 (9-10) :6531-6545
[22]   Effects of small additions of Zn on the microstructure, mechanical properties and corrosion resistance of WE43B Mg alloys [J].
Koltygin, A., V ;
Bazhenov, V. E. ;
Khasenova, R. S. ;
Komissarov, A. A. ;
Bazlov, A., I ;
Bautin, V. A. .
INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2019, 26 (07) :858-868
[23]   New insights on the high-corrosion resistance of UHP Mg-Ge alloys tested in a simulated physiological environment [J].
Liu, Ting ;
Chen, Xingrui ;
Venezuela, Jeffrey ;
Wang, Yuan ;
Shi, Zhiming ;
Chen, Wenyi ;
Dargusch, Matthew .
JOURNAL OF MAGNESIUM AND ALLOYS, 2024, 12 (03) :1026-1044
[24]   Effect of recrystallisation annealing on grain refinement for superplastic forming of cold-rolled aluminium alloy 5083 [J].
Yagodzinskyy, Y ;
Pimenoff, J ;
Romu, J ;
Tarasenko, O ;
Hänninen, H .
ADVANCES IN MECHANICAL BEHAVIOUR, PLASTICITY AND DAMAGE, VOLS 1 AND 2, PROCEEDINGS, 2000, :275-280
[25]   Forming of magnesium alloys at 100 °C by hydrostatic extrusion [J].
Swiostek, J. ;
Goeken, J. ;
Letzig, D. ;
Kainer, K. U. .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2006, 15 (06) :705-711
[26]   Forming of magnesium alloys at 100 °C by hydrostatic extrusion [J].
J. Swiostek ;
J. Göken ;
D. Letzig ;
K. U. Kainer .
Journal of Materials Engineering and Performance, 2006, 15 :705-711
[27]   Microstructure and Superplastic Behavior of Ni-Modified Ti-Al-Mo-V Alloys [J].
Kotov, Anton D. ;
Postnikova, Maria N. ;
Mosleh, Ahmed O. ;
Cheverikin, Vladimir V. ;
Mikhaylovskaya, Anastasia, V .
METALS, 2022, 12 (05)
[28]   Severe Plastic Deformation of Mg-Zn-Zr-Ce Alloys: Advancing Corrosion Resistance and Mechanical Strength for Medical Applications [J].
Luginin, Nikita ;
Eroshenko, Anna ;
Khimich, Margarita ;
Prosolov, Konstantin ;
Kashin, Alexander ;
Uvarkin, Pavel ;
Tolmachev, Alexey ;
Glukhov, Ivan ;
Panfilov, Alexander ;
Sharkeev, Yurii .
METALS, 2023, 13 (11)
[29]   Engineering Corrosion Resistance in Magnesium Alloys for Biomedical Applications: A Synergy of Zn/Ca Atomic Ratio and Texture-Based Approach [J].
Behera, Manisha ;
Shabadi, Rajashekhara ;
Gruescu, Cosmin .
METALS, 2024, 14 (09)
[30]   INDENTATION RESISTANCE AND CORROSION BEHAVIOUR OF Fe-Mn MODIFIED Cu-Al ALLOYS IN SELECTED INDUSTRIAL AND BIOLOGICAL FLUIDS [J].
Alaneme, Kenneth Kanayo .
ACTA METALLURGICA SLOVACA, 2014, 20 (04) :366-373
12345