INHIBITORY ACTION OF GARLIC EXTRACT IN THE CORROSION OF COPPER UNDER THIN ELECTROLYTE LAYERS

被引：3
|
作者：
Chen, Zhenyu [1 ,2 ]
Cen, Hongyu [1 ]
Wei, Lisha [1 ]
Cao, Yamin [1 ]
Guo, Xingpeng [1 ,2 ]
机构：
[1] Huazhong Univ Sci & Technol, Sch Chem & Chem Engn, Minist Educ, Key Lab Mat Chem Energy Convers & Storage, Wuhan 430074, Hubei, Peoples R China
[2] Huazhong Univ Sci & Technol, Sch Chem & Chem Engn, Hubei Key Lab Mat Chem & Serv Failure, Wuhan 430074, Hubei, Peoples R China
来源：
SURFACE REVIEW AND LETTERS | 2019年 / 26卷 / 01期
基金：
中国国家自然科学基金;
关键词：
Garlic extracts; atmospheric corrosion; inhibitor; XPS; X-RAY PHOTOELECTRON; ORGANOSULFUR CONSTITUENTS; ATMOSPHERIC CORROSION; CARBON-STEEL; SURFACE; SPECTROSCOPY; RESPONSES; BEHAVIOR; PHASE; OIL;
D O I：
10.1142/S0218625X18501287
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The inhibition effects of garlic extract on copper corrosion under a thin electrolyte layer (TEL) were investigated using weight-loss measurements, electrochemical methods and surface analysis. Results showed that the volatile organosulfur compounds of garlic extract, such as diallyl trisulfide and di-2-propenyl disulfide, among others, could adsorb on the surface of copper and have a significant inhibitory effect on copper corrosion. Garlic extract acted as a mixed-type inhibitor for copper under TEL. Surface analyses, such as scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS), were conducted to illustrate the inhibitive mechanisms of this plant extract under a TEL.
引用
收藏
页数：9
相关论文
共 50 条
  • [1] Benzotriazole as a volatile corrosion inhibitor during the early stage of copper corrosion under adsorbed thin electrolyte layers
    Chen, Zhenyu
    Huang, Ling
    Zhang, Guoan
    Qiu, Yubing
    Guo, Xingpeng
    CORROSION SCIENCE, 2012, 65 : 214 - 222
  • [2] The corrosion of tin under thin electrolyte layers containing chloride
    Zhong, Xiankang
    Zhang, Guoan
    Qiu, Yubin
    Chen, Zhenyu
    Guo, Xingpeng
    Fu, Chaoyang
    CORROSION SCIENCE, 2013, 66 : 14 - 25
  • [3] Models for Corrosion of Metals under Thin Electrolyte Layers
    Venkatraman, M. S.
    Bosco, I. G.
    Cole, I. S.
    Emmanuel, B.
    CORROSION (GENERAL) - 219TH ECS MEETING, 2011, 35 (17): : 1 - 10
  • [4] Corrosion behavior of 907 steel under thin electrolyte layers of artificial seawater
    王慧萍
    丁少春
    朱娟
    张昭
    张鉴清
    曹楚南
    JournalofCentralSouthUniversity, 2015, 22 (03) : 806 - 814
  • [5] Corrosion behavior of 907 steel under thin electrolyte layers of artificial seawater
    Wang Hui-ping
    Ding Shao-chun
    Zhu Juan
    Zhang Zhao
    Zhang Jian-qing
    Cao Chu-nan
    JOURNAL OF CENTRAL SOUTH UNIVERSITY, 2015, 22 (03) : 806 - 814
  • [6] Corrosion behavior of 907 steel under thin electrolyte layers of artificial seawater
    Hui-ping Wang
    Shao-chun Ding
    Juan Zhu
    Zhao Zhang
    Jian-qing Zhang
    Chu-nan Cao
    Journal of Central South University, 2015, 22 : 806 - 814
  • [7] Effect of an alternating electric field on the atmospheric corrosion behaviour of copper under a thin electrolyte layer
    Huang, Hualiang
    Pan, Zhiquan
    Guo, Xingpeng
    Qiu, Yubing
    CORROSION SCIENCE, 2013, 75 : 100 - 105
  • [8] Corrosion behavior of immersion silver printed circuit board copper under a thin electrolyte layer
    Huang, Hualiang
    Guo, Xiaomeng
    Bu, Furong
    Huang, Gangliang
    ENGINEERING FAILURE ANALYSIS, 2020, 117
  • [9] Pitting Corrosion of Silica-Coated Type 304 Stainless Steel Under Thin Electrolyte Layers
    Maier, B.
    Frankel, G. S.
    CORROSION, 2011, 67 (03)
  • [10] 2-Propynylamine as a Vapor Corrosion Inhibitor for Carbon Steel under Adsorbed Thin Electrolyte Layers
    Chen, Juan
    Chen, Zhenyu
    Guo, Xingpeng
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2014, 161 (03) : C151 - C155
12345