Structure and photoactivity of titania derived from nanotubes and nanofibers

被引：44

作者：

Inagaki, Michio ^{[1
]}

Kondo, Naho ^{[1
]}

Nonaka, Rie ^{[1
]}

Ito, Eiki ^{[2
]}

Toyoda, Masahiro ^{[3
]}

Sogabe, Kazuo ^{[3
]}

Tsumura, Tomoki ^{[2
]}

机构：

[1] Aichi Inst Technol, Fac Engn, Toyota 4700392, Japan

[2] Nard Inst Ltd, Amagasaki, Hyogo 6600805, Japan

[3] Oita Univ, Fac Engn, Oita 8701192, Japan

来源：

JOURNAL OF HAZARDOUS MATERIALS | 2009年 / 161卷 / 2-3期

关键词：

Titania nanotube; Photoactivity; Annealing; Crystallinity; Adsorptivity; PHOTOCATALYTIC ACTIVITY; ANATASE POWDERS; MICROSTRUCTURES; OXIDATION; LAYER;

D O I：

10.1016/j.jhazmat.2008.05.003

中图分类号：

X [环境科学、安全科学];

学科分类号：

08 ; 0830 ;

摘要：

Photoactivity under UV irradiation for the decomposition of methylene blue in water and for the oxidation of NO gas was studied on titania powders derived from titanate nanotube (TNT) and nanofiber (TNF) by annealing at high temperatures, comparing with granular titania (ST-01). Rate constant for methylene blue decomposition k(MB) increased with increasing annealing temperature above 300 degrees C after the conversion from titanate to tinania. It tended to decrease above 700 degrees C, mainly due to the phase transformation from anatase to rutile. The dependences of k(MB) on full width at half maximum intensity (FWHM) were common for three samples, a sharp maximum at around 0.4 degrees in FWHM, but TNF-derived sample gave much higher maximum than ST-01. Change in fraction of oxidized NO with annealing temperature showed a plateau at around 50% and then decreased abruptly by high temperature annealing. Starting from TNT and TNF has an advantage to form fine particles by annealing above 300 degrees C, giving high photoactivity due to high crystallinity and high adsorptivity particularly for methylene blue. (c) 2008 Elsevier B.V. All rights reserved.

引用

页码：1514 / 1521

页数：8

共 24 条

[1] Protonated titanates and TiO2 nanostructured materials:: Synthesis, properties, and applications [J].

Bavykin, Dmitry V. ;

Friedrich, Jens M. ;

Walsh, Frank C. .

ADVANCED MATERIALS, 2006, 18 (21) :2807-2824

[2] The structure of trititanate nanotubes [J].

Chen, Q ;

Du, GH ;

Zhang, S ;

Peng, LM .

ACTA CRYSTALLOGRAPHICA SECTION B-STRUCTURAL SCIENCE, 2002, 58 :587-593

[3] In situ thermo-Raman study of titanium oxide nanotubes [J].

Cortes-Jacome, M. A. ;

Ferrat-Torres, G. ;

Ortiz, L. F. Flores ;

Angeles-Chavez, C. ;

Lopez-Salinas, E. ;

Escobar, J. ;

Mosqueira, M. L. ;

Toledo-Antonio, J. A. .

CATALYSIS TODAY, 2007, 126 (1-2) :248-255

[4] Preparation and structure analysis of titanium oxide nanotubes [J].

Du, GH ;

Chen, Q ;

Che, RC ;

Yuan, ZY ;

Peng, LM .

APPLIED PHYSICS LETTERS, 2001, 79 (22) :3702-3704

[5] Carbon-coated anatase: the role of the carbon layer for photocatalytic performance [J].

Inagaki, M ;

Kojin, F ;

Tryba, B ;

Toyoda, M .

CARBON, 2005, 43 (08) :1652-1659

[6] Photocatalytic activity of anatase powders for oxidation of methylene blue in water and diluted NO gas [J].

Inagaki, M ;

Imai, T ;

Yoshikawa, T ;

Tryba, B .

APPLIED CATALYSIS B-ENVIRONMENTAL, 2004, 51 (04) :247-254

[7] Dependence of photocatalytic activity of anatase powders on their crystallinity [J].

Inagaki, Michio ;

Nonaka, Rie ;

Tryba, Beata ;

Morawski, Antoni W. .

CHEMOSPHERE, 2006, 64 (03) :437-445

[8]

Jung JH, 2002, CHEM MATER, V14, P1445, DOI 10.1021/cmOI1625

[9] Formation of titanium oxide nanotube [J].

Kasuga, T ;

Hiramatsu, M ;

Hoson, A ;

Sekino, T ;

Niihara, K .

LANGMUIR, 1998, 14 (12) :3160-3163

[10]

Kasuga T, 1999, ADV MATER, V11, P1307, DOI 10.1002/(SICI)1521-4095(199910)11:15<1307::AID-ADMA1307>3.0.CO

← 1 2 3 →