Fracture behaviour of PC/ABS resin under mixed-mode loading

Fracture behaviour of polycarbonate (PC)/acrylonitrile-butadiene-styrene (ABS) under mixed-mode loading conditions was studied for several weight fractions of PC and ABS. Mode I and mixed-mode fracture tests were carried out by using compact-tension-shear specimens. At a certain value of mixed-mode loading ratio K-II/K-I a crack of the shear type will initiates at the initial crack tip. Fracture toughness increases under mixed-mode loading with an increase in the mode II component, whereas it reduces with the appearance of a shear-type fracture. Fracture toughness and the appearance of a shear-type fracture depends on the blending ratio of PC and ABS. The transition to shear-type fracture occurs at lower value of K-II/K-I, for resins with higher fracture toughness.