Low temperature synthesis of hydroxyapatite from CaHPO4•2H2O and Ca(OH)2 based on effect of the spark plasma system (SPS)

被引：10
|
作者：
Omori, Mamoru
Onoki, Takamasa
Hashida, Toshiyuki
Okubo, Akira
Murakami, Yoshihiro
机构：
[1] Tohoku Univ, Fracture & Reliabil Res Inst, Grad Sch Engn, Aoba Ku, Sendai, Miyagi 9808579, Japan
[2] Tohoku Univ, Inst Mat Res, Aoba Ku, Sendai, Miyagi 9808577, Japan
来源：
CERAMICS INTERNATIONAL | 2006年 / 32卷 / 06期
关键词：
hydroxyapatite; hydroxyapatite synthesis; spark plasma system (SPS); spark plasma sintering (SPS); calcium phosphate;
D O I：
10.1016/j.ceramint.2005.04.021
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
A mixture of 6 mol of CaHPO4 center dot 2H(2)O and 4 mol of Ca(OH)(2) was reacted to produce hydroxyapatite (HA) by spark plasma system (SPS). The reaction was carried out at 300-1200 degrees C under pressure of 20-670 MPa for 10 min in a vacuum. HA formation started at 300 degrees C at 600 MPa and was completed at 500 degrees C at 670 MPa, the same product being obtained at 1200 degrees C in air using a furnace. The temperature of the HA formation increased with decreasing pressure and was 1150 degrees C under 20 MPa. There was a linear relationship between the reaction temperature and pressure. The crystal size of the HA prepared at 500 degrees C at 670 MPa and that at 600 degrees C at 600 MPa by SPS were less than 1 and 2 mu m, respectively. (C) 2005 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
引用
收藏
页码：617 / 621
页数：5
相关论文
共 50 条
  • [31] In situ microemulsion synthesis of hydroxyapatite-MgFe2O4 nanocomposite as a magnetic drug delivery system
    Foroughi, Firoozeh
    Hassanzadeh-Tabrizi, S. A.
    Bigham, Ashkan
    MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS, 2016, 68 : 774 - 779
  • [32] The effect of temperature on the in situ synthesis-sintering and mechanical properties of MoSi2 prepared by spark plasma sintering
    Kermani, Milad
    Razavi, Mansour
    Rahimipour, Mohammad Reza
    Zakeri, Mohammad
    JOURNAL OF ALLOYS AND COMPOUNDS, 2014, 585 : 229 - 233
  • [33] Spark plasma sintering (SPS) consolidated ceramic composites from plasma-sprayed metastable Al2TiO5 powder and nano-Al2O3, TiO2, and MgO powders
    Duan, RG
    Zhan, GD
    Kuntz, JD
    Kear, BH
    Mukherjee, AK
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 373 (1-2): : 180 - 186
  • [34] Obtaining Ca(H2PO4)2•H2O, monocalcium phosphate monohydrate, via monetite from brushite by using sonication
    Sanchez-Enriquez, J.
    Reyes-Gasga, J.
    ULTRASONICS SONOCHEMISTRY, 2013, 20 (03) : 948 - 954
  • [35] In vitro evaluation of bone regeneration and drug release properties of a silver nanoparticles-coated ferromagnetic hydroxyapatite {Fe2O3-NiO-Ca10(PO4)(OH)2} system
    Anand, Vikas
    Heera, Pawan
    Kumar, Mukesh
    Sharma, Aakriti
    Thakur, Sourbh
    JOURNAL OF MATERIALS RESEARCH, 2024, : 213 - 222
  • [36] The effect of plaster (CaSO4•1/2H2O) on the compressive strength, self-setting property, and in vitro bioactivity of silicate-based bone cement
    Liu, Wenjuan
    Wu, Chengtie
    Liu, Weining
    Zhai, Wanyin
    Chang, Jiang
    JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART B-APPLIED BIOMATERIALS, 2013, 101B (02) : 279 - 286
  • [37] Brushite (Ca,M)HPO4, 2H2O doping with bioactive ions (M = Mg2+, Sr2+, Zn2+, Cu2+, and Ag+): a new path to functional biomaterials?
    Sayahi, M.
    Santos, J.
    El-Feki, H.
    Charvillat, C.
    Bosc, F.
    Karacan, I
    Milthorpe, B.
    Drouet, C.
    MATERIALS TODAY CHEMISTRY, 2020, 16 (16)
  • [38] Rational design of highly H2O- and CO2-tolerant hydroxyapatite-supported Pd catalyst for low-temperature methane combustion
    Zhang, Yangyu
    Zhu, Jie
    Li, Shusheng
    Xiao, Yihong
    Zhan, Yingying
    Wang, Xiuyun
    Au, Chak-tong
    Jiang, Lilong
    CHEMICAL ENGINEERING JOURNAL, 2020, 396
  • [39] Effect of Al2O3, SiO2 and carbon nanotubes on the microstructural and mechanical behavior of spark plasma sintered aluminum based nanocomposites
    Sadeghi, B.
    Cavaliere, P.
    Perrone, A.
    PARTICULATE SCIENCE AND TECHNOLOGY, 2020, 38 (01) : 7 - 14
  • [40] Stability analysis of hydroxyapatite in the system P-Ca-H2O aided prediction of the mechanisms of dephosphorization from the high phosphorus iron ore by hydrometallurgy process
    Zhou, Xuejiao
    Xia, Wentang
    Chen, Yongli
    Yin, Jianguo
    Yuan, Xiaoli
    METALLURGICAL RESEARCH & TECHNOLOGY, 2016, 113 (03)
12345