Low temperature synthesis of hydroxyapatite from CaHPO4•2H2O and Ca(OH)2 based on effect of the spark plasma system (SPS)

被引：10
|
作者：
Omori, Mamoru
Onoki, Takamasa
Hashida, Toshiyuki
Okubo, Akira
Murakami, Yoshihiro
机构：
[1] Tohoku Univ, Fracture & Reliabil Res Inst, Grad Sch Engn, Aoba Ku, Sendai, Miyagi 9808579, Japan
[2] Tohoku Univ, Inst Mat Res, Aoba Ku, Sendai, Miyagi 9808577, Japan
来源：
CERAMICS INTERNATIONAL | 2006年 / 32卷 / 06期
关键词：
hydroxyapatite; hydroxyapatite synthesis; spark plasma system (SPS); spark plasma sintering (SPS); calcium phosphate;
D O I：
10.1016/j.ceramint.2005.04.021
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
A mixture of 6 mol of CaHPO4 center dot 2H(2)O and 4 mol of Ca(OH)(2) was reacted to produce hydroxyapatite (HA) by spark plasma system (SPS). The reaction was carried out at 300-1200 degrees C under pressure of 20-670 MPa for 10 min in a vacuum. HA formation started at 300 degrees C at 600 MPa and was completed at 500 degrees C at 670 MPa, the same product being obtained at 1200 degrees C in air using a furnace. The temperature of the HA formation increased with decreasing pressure and was 1150 degrees C under 20 MPa. There was a linear relationship between the reaction temperature and pressure. The crystal size of the HA prepared at 500 degrees C at 670 MPa and that at 600 degrees C at 600 MPa by SPS were less than 1 and 2 mu m, respectively. (C) 2005 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
引用
收藏
页码：617 / 621
页数：5
相关论文
共 50 条
  • [1] Formation of needle-like hydroxyapatite by hydrothermal treatment of CaHPO4•2H2O combined with β-Ca3(PO4)2
    Watanabe, Tomoko
    Kawachi, Giichiro
    Kamitakahara, Masanobu
    Kikuta, Koichi
    Ohtsuki, Chikara
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2009, 117 (1366) : 759 - 764
  • [2] Synthesis and Characterization of New Copper(II) Substituted Dicalcium Phosphate Dihydrate (CaHPO4•2H2O)
    El Hamidi, A.
    Halim, M.
    Arsalane, S.
    Kacimi, M.
    Ziyad, M.
    ASIAN JOURNAL OF CHEMISTRY, 2012, 24 (06) : 2698 - 2702
  • [3] Electroless deposition of brushite (CaHPO4•2H2O) crystals on Ti-6Al-4V at room temperature
    Tas, A. Cuneyt
    INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2006, 97 (05) : 639 - 644
  • [4] AFM study of the epitaxial growth of brushite (CaHPO4•2H2O) on gypsum cleavage surfaces
    Jorge Pinto, Andre
    Ruiz-Agudo, Encarnacion
    Putnis, Christine V.
    Putnis, Andrew
    Jimenez, Amalia
    Prieto, Manuel
    AMERICAN MINERALOGIST, 2010, 95 (11-12) : 1747 - 1757
  • [5] Effects of magnesium on the formation of calcium-deficient hydroxyapatite from CaHPO4 center dot 2H(2)O and Ca-4(PO4)(2)O
    TenHuisen, KS
    Brown, PW
    JOURNAL OF BIOMEDICAL MATERIALS RESEARCH, 1997, 36 (03): : 306 - 314
  • [6] Brushite (CaHPO4•2H2O) to octacalcium phosphate (Ca8(HPO4)2(PO4)4•5H2O) transformation in DMEM solutions at 36.5 °C
    Mandel, Selen
    Tas, A. Cuneyt
    MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS, 2010, 30 (02): : 245 - 254
  • [7] Influence of some foreign metal ions on crystal growth kinetics of brushite (CaHPO4•2H2O)
    Rosa, Silvia
    Madsen, Hans E. Lundager
    JOURNAL OF CRYSTAL GROWTH, 2010, 312 (20) : 2983 - 2988
  • [8] Synthesis and characterization of hydroxyapatite by microwave heating using CaSO4•2H2O and Ca(OH)2 as calcium source
    Teoreanu, Ion
    Preda, Maria
    Melinescu, Alina
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN MEDICINE, 2008, 19 (02) : 517 - 523
  • [9] Synthesis and characterization of hydroxyapatite by microwave heating using CaSO4·2H2O and Ca(OH)2 as calcium source
    Ion Teoreanu
    Maria Preda
    Alina Melinescu
    Journal of Materials Science: Materials in Medicine, 2008, 19 : 517 - 523
  • [10] Mechanochemical Synthesis of Nanocrystalline Hydroxyapatite from Ca(H2PO4)2.H2O, CaO, Ca(OH)2, and P2O5 Mixtures
    Dinda, Sneha
    Bhagavatam, Ajay
    Alrehaili, Husam
    Dinda, Guru Prasad
    NANOMATERIALS, 2020, 10 (11) : 1 - 10
12345