Temperature-Programmed Surface Reaction Study of Adsorption and Reaction of H2S on Ceria

被引：2
作者：
Liu Bing [1 ,2 ,3 ]
Xu Hengyong [1 ]
Zhang Zehui [2 ,3 ]
机构：
[1] Chinese Acad Sci, Dalian Inst Chem Phys, Dalian 116023, Liaoning, Peoples R China
[2] S Cent Univ Nationalities, Coll Chem & Mat Sci, Key Lab Catalysis & Mat Sci, State Ethn Affairs Commiss, Wuhan 430074, Hubei, Peoples R China
[3] S Cent Univ Nationalities, Coll Chem & Mat Sci, Minist Educ, Wuhan 430074, Hubei, Peoples R China
来源：
CHINESE JOURNAL OF CATALYSIS | 2012年 / 33卷 / 10期
关键词：
ceria; hydrogen sulfide; adsorption; temperature-programmed surface reaction; GAS-SHIFT REACTION; HYDROGEN-SULFIDE; SULFUR; CATALYSTS; REMOVAL;
D O I：
10.1016/S1872-2067(11)60416-6
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
H2S adsorption and reaction on CeO2, TiO2, and gamma-Al2O3 were studied by temperature programmed surface reaction (TPSR). Ceria had the best desulfidation ability. The pretreatment atmosphere affected H2S adsorption and reaction on ceria, and desulfidation efficiency increased in the order of inert atmosphere, reducing atmosphere, oxidizing atmosphere. H2S was first adsorbed on pretreated ceria at room temperature. On increasing the temperature in an Ar (99.99%) atmosphere, part of the H2S desorbed below 673 K, and another part reacted with the surface oxygen on ceria to produce sulfur and water below 473 K, and SO2 between 473 and 673 K, which further reacted with lattice oxygen and was transformed into sulfate above 673 K. The sulfate decomposed into SO2 again at 873 K. To avoid the complex regeneration, it is advisable to carry out desulfidation below 673 K when using ceria as adsorbent.
引用
收藏
页码：1631 / 1635
页数：5
相关论文
共 50 条
  • [41] First principles study of H2S adsorption and dissociation on Fe(110)
    Jiang, DE
    Carter, EA
    SURFACE SCIENCE, 2005, 583 (01) : 60 - 68
  • [42] H2S adsorption on polycrystalline UO2
    Wu, QF
    Yakshinskiy, BV
    Gouder, T
    Madey, TE
    CATALYSIS TODAY, 2003, 85 (2-4) : 291 - 301
  • [43] Chitosan Biocomposites for the Adsorption and Release of H2S
    Batista, Mary
    Pinto, Moises L.
    Antunes, Fernando
    Pires, Joao
    Carvalho, Silvia
    MATERIALS, 2021, 14 (21)
  • [44] Surface neutralization and H2S oxidation at early stages of sewer corrosion: Influence of temperature, relative humidity and H2S concentration
    Joseph, Antony P.
    Keller, Juerg
    Bustamante, Heriberto
    Bond, Philip L.
    WATER RESEARCH, 2012, 46 (13) : 4235 - 4245
  • [45] Insight into the adsorption and decomposition mechanism of H2S on clean and S-covered Au (100) surface: A theoretical study
    Jiang, Zhao
    Li, Mengmeng
    Qin, Pei
    Fang, Tao
    APPLIED SURFACE SCIENCE, 2014, 311 : 40 - 46
  • [46] Effects of coverage and solvent on H2S adsorption on the Cu(100) surface: A DFT study
    Chen, Shenghui
    Sun, Shuangqing
    Ma, Yunfei
    Lian, Bingjie
    Hu, Songqing
    SURFACE AND INTERFACE ANALYSIS, 2015, 47 (05) : 565 - 571
  • [47] Thermodynamic Reaction Study of Conversion of H2S and CO2 and the Promoting Effect of Light on the Reaction
    Duan, Yuangang
    Yu, Shan
    He, Zhen
    Huang, Jingyuan
    Wang, Fushen
    Fu, Mengyao
    Huang, Zeai
    Zhou, Ying
    CHEMPHOTOCHEM, 2024, 8 (12):
  • [48] H2S adsorption and decomposition on the gradually reduced α-Fe2O3(001) surface: A DFT study
    Lin, Changfeng
    Qin, Wu
    Dong, Changqing
    APPLIED SURFACE SCIENCE, 2016, 387 : 720 - 731
  • [49] Dynamic Adsorption of H2S onto a Goethite-Based Material
    Jose Alguacil, Francisco
    Angel Alonso, Manuel
    Antonio Lopez, Felix
    Ignacio Robla, Jose
    MOLECULES, 2022, 27 (22):
  • [50] Adsorption of hydrogen sulfide (H2S) on zeolite (Z): Retention mechanism
    Sigot, Lea
    Ducom, Gaelle
    Germain, Patrick
    CHEMICAL ENGINEERING JOURNAL, 2016, 287 : 47 - 53
12345