Direct synthesis of B-C-N single-walled nanotubes by bias-assisted hot filament chemical vapor deposition

Direct synthesis of large-scale ternary boron carbonitride single-walled nanotubes (BCN-SWNTs) via a bias-assisted HFCVD process was presented. The BCN-SWNTs were grown over the powdery Fe-Mo/MgO catalyst by using CH4, B2H6, and ethylenediamine vapor as the reactant gases. As high as 16 atom % nitrogen can be incorporated within the nanotube shells, with the boron content in the range of 2-4 atom %. The ternary covalent bonding nature of the BCN-SWNTs was well characterized, and the B, C, and N elemental maps were clearly imaged by energy-filtered transmission electron microscopy. Copyright © 2006 American Chemical Society.