Microstructure and Wear-Resistant Properties of Ni80Al20-MoS2Composite Coating on Sled Track Slippers

In order to increase the surface hardness and wear-resistance property of sled track slippers, a Ni80Al20-MoS(2)composite coating was fabricated on the surface of a stainless steel 0Cr18Ni9Ti sled track slipper via atmospheric spray and hot dipping. The microstructure, composition and surface hardness of coatings under different spraying powers were characterized and measured. The wear-resistant properties of the slipper substrate and the coating were also checked. The results showed that the higher the spraying power was, the greater the smoothness, density and hardness was of the Ni80Al20 coating, while the thickness initially increased and then decreased. When the spraying power was 18 kW, the thickness was 342.5 mu m, the surface hardness was 304.1 Hv(0.2), and the coating was composed of Ni, Al, Ni3Al, NiAl and a little Al2O3. The friction coefficient of the slipper substrate against GCr15 balls at room temperature in air was 0.7, while the coated substrate with MoS(2)lubrication film was 0.3 and the volume wear rate declined by 1/5. The friction coefficient of the Ni80Al20 coating was 0.5 and the Ni80Al20-MoS(2)composite coating was 0.15, while the volume wear rate declined by 1/4 and 1/3.