Interpretation of creep crack growth data for 1/2 CMV steel weldments

被引:1
作者
Ejaz, Muneeb [1 ]
Davies, Catrin M. [1 ]
Dean, David W. [2 ]
机构
[1] Imperial Coll London, Dept Mech Engn, South Kensington Campus, London SW7 2AZ, England
[2] EDF Energy Generat Ltd, Barnwood GL4 3RS, Glos, England
来源
21ST EUROPEAN CONFERENCE ON FRACTURE, (ECF21) | 2016年 / 2卷
关键词
creep crack growth; 1/2CMV; K-mat(c); Weldments; Heat affected zone (HAZ); FAILURE ASSESSMENT DIAGRAM; INITIATION;
D O I
10.1016/j.prostr.2016.06.116
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
1/2Cr1/2Mo1/4V (1/2CMV) steel has been used in high temperature power plant piping due to its enhanced weld properties. Creep crack growth testing has been performed on compact tension C(T) specimens of 1/2CMV (low alloy ferritic) steel at 540 degrees C on both parent metal specimens as well as fine and coarse grained heat affected zone (HAZ) specimens, where the initial crack is located within the HAZ. The data has been interpreted using the fracture mechanics parameter C* against the crack growth rate. The creep toughness parameter, K-mat(c), is also evaluated for the material. It was seen that, for a given C* value, the fine grained HAZ material generally exhibits higher crack growth rates than the post weld heat treated coarse grained HAZ. Copyright (C) 2016 The Authors. Published by Elsevier B.V.
引用
收藏
页码:903 / 910
页数:8
相关论文
共 12 条
[1]  
[Anonymous], 1992, P192 ESIS
[2]  
ASTM, 2013, STAND TEST METH LIN, P1, DOI [10.1520/E0399-12E03.2, DOI 10.1520/E0399-12E03.2]
[3]  
ASTM, 2015, STAND TEST METH MEAS, DOI [10.1520/E1457-07E04.2, DOI 10.1520/E1457-07E04.2.BAKER]
[4]  
Baker A., 2004, TECHNICAL REPORT
[5]   Use of the R5 volume 4/5 procedures to assess creep-fatigue crack growth in a 316L(N) cracked plate at 650 °C [J].
Baker, AJ ;
O'Donnell, MP ;
Dean, DW .
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2003, 80 (7-8) :481-488
[6]  
BEGL, 2003, TECHNICAL REPORT
[7]   Predicting creep crack initiation in austenitic and ferritic steels using the creep toughness parameter and time-dependent failure assessment diagram [J].
Davies, C. M. .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2009, 32 (10) :820-836
[8]   Failure assessment diagram analysis of creep crack initiation in 316H stainless steel [J].
Davies, CM ;
O'Dowd, NP ;
Dean, DW ;
Nikbin, KM ;
Ainsworth, RA .
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2003, 80 (7-8) :541-551
[9]  
DAVIES CM, 2006, J ASTM INT, V3, DOI DOI 10.1520/JAI13221
[10]  
Gladwin D. N., 2000, INTERNAL REPORT CREE