PRETREATMENT OF MOSO BAMBOO WITH DILUTE PHOSPHORIC ACID

Dilute phosphoric acid pretreatment of moso bamboo materials was studied for producing high quality dissolving pulp for textile applications. The dynamics of dilute acid pretreatment were considered. The Saeman model was found to describe well the acid hydrolysis of moso bamboo hemicelluloses to their monomers under different temperatures and different dilute phosphoric acid concentrations. The initial degradation rate of hemicelluloses was much higher than its subsequent degradation rate, and the xylose generation rate increased with increasing temperature. The change rule of the pentose extraction rate was considered along with the pretreatment factor (P factor). Optimum dilute acid pretreatment conditions were 170 degrees C and 45 minutes. Based on the optimum conditions and a mass balance of sugars, a weight loss of 26.5% of the solid and liquid fractions combined was observed after the pretreatment. SEM results revealed that the moso bamboo fibers surfaces and cell wall were damaged. With the surface area increasing, the accessible pore areas also increased. At the same time, the crystallinity of the cellulose was reduced, which created a favorable environment for chemical penetration in the subsequent treatment.