Microstructure and texture evolution of a cold rolled Ni-Cr-W alloy after annealing

被引：1
|
作者：
Wang, W. [1 ]
Drouelle, I. [1 ]
Brisset, F. [1 ]
Mathon, M. H. [2 ]
Auger, T. [3 ]
Baudin, T. [1 ]
机构：
[1] Univ Paris 11, CNRS, ICMMO, UMR 8182, F-91405 Orsay, France
[2] CEA Saclay, CNRS CEA, Leon Brillouin Lab, F-92290 Chatenay Malabry, France
[3] CNRS, UMR 8579, MSSMAT, ECP, F-92290 Chatenay Malabry, France
来源：
TEXTURES OF MATERIALS, PTS 1 AND 2 | 2012年 / 702-703卷
关键词：
Texture; Microstructure; Cold rolling; Annealing; EBSD; Neutron diffraction; Ni-Cr-W alloy; RECRYSTALLIZATION TEXTURES;
D O I：
10.4028/www.scientific.net/MSF.702-703.352
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A Ni-5.7%Cr-25.2%W (wt%) alloy was deformed by cold rolling in different reduction conditions (50%, 70%, and 90%) and then annealed under hydrogen atmosphere. Microstructure and texture evolutions were analyzed using Electron Back Scattered Diffraction (EBSD). Orientation Distribution Functions (ODFs) and stored energy were calculated from neutron diffraction measurements. A strengthening of the a-fiber texture was observed after 90% cold rolling and a homogenous microstructure was obtained after annealing at 900 degrees C.
引用
收藏
页码：352 / +
页数：2
相关论文
共 50 条
  • [1] Microstructure and texture evolution in cold-rolled W during annealing
    Liu, Wenbin
    Zhang, Wen
    Li, Jianfeng
    Xu, Hailong
    Liu, Hui
    Xia, Mingxing
    Li, Yanchao
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2024, 123
  • [2] Processes leading to formation of cube texture in cold-rolled Ni-Cr-W alloy
    Dosovitskiy, G. A.
    Mudretsova, S. N.
    Garshev, A. V.
    Amelichev, V. A.
    Samoilenkov, S. V.
    Gervasieva, I. V.
    Khlebnikova, Yu. V.
    Rodionov, D. P.
    Kaul, A. R.
    PHYSICS OF METALS AND METALLOGRAPHY, 2014, 115 (01) : 30 - 38
  • [3] Processes leading to formation of cube texture in cold-rolled Ni-Cr-W alloy
    G. A. Dosovitskiy
    S. N. Mudretsova
    A. V. Garshev
    V. A. Amelichev
    S. V. Samoilenkov
    I. V. Gervasieva
    Yu. V. Khlebnikova
    D. P. Rodionov
    A. R. Kaul
    The Physics of Metals and Metallography, 2014, 115 : 30 - 38
  • [4] Microstructure and Texture Evolution of Cu-Ni-P Alloy after Cold Rolling and Annealing
    Yang, Wendi
    Zhang, Chengzhi
    Zhang, Nan
    Zhang, Chucan
    Gao, Weilin
    He, Jilin
    MATERIALS, 2024, 17 (11)
  • [5] Microstructure and texture evolution of cold rolled 1070 Al alloy during the subsequent annealing treatment
    Wang, Qing
    Yang, Peng
    Zhang, Baorui
    Fan, Hui
    Xu, Xuexia
    Li, Wenbin
    Fan, Xiaoliang
    Wang, Jinfeng
    Ding, Haimin
    RESULTS IN PHYSICS, 2019, 13
  • [6] Effect of annealing on the microstructure and texture of cold rolled CrCoNi medium-entropy alloy
    Sathiaraj, G. Dan
    Skrotzki, Werner
    Pukenas, Aurimas
    Schaarschuch, Rolf
    Immanuel, R. Jose
    Panigrahi, S. K.
    Chelvane, J. Arout
    Kumar, S. S. Satheesh
    INTERMETALLICS, 2018, 101 : 87 - 98
  • [7] Evolution of microstructure and texture during cold rolling and high-temperature annealing in Ni-5 at% W substrate for coated conductor
    Chen, Xing-Pin
    Chen, Dan
    Sun, Hong-Fu
    Wang, Li-Xia
    Shang, Du
    RARE METALS, 2020, 39 (08) : 928 - 935
  • [8] Texture and microstructure evolution in cold rolled AZ31 magnesium alloy
    Chang, L. L.
    Shang, E. F.
    Wang, Y. N.
    Zhao, X.
    Qi, M.
    MATERIALS CHARACTERIZATION, 2009, 60 (06) : 487 - 491
  • [9] Texture Evolution in Heavily Cold-Rolled FeCo-2V Alloy during Annealing
    Deng, Jiangning
    Yang, Yanling
    Wang, Yandong
    Chen, Jingeng
    Peng, Rulin
    Yuan, Chenchen
    Bouzy, Emmanuel
    Fundenberger, Jean-Jacques
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2009, 25 (02) : 219 - 224
  • [10] Evolution of microstructure and texture during cold rolling and high-temperature annealing in Ni–5 at% W substrate for coated conductor
    Xing-Pin Chen
    Dan Chen
    Hong-Fu Sun
    Li-Xia Wang
    Du Shang
    Rare Metals, 2020, 39 : 928 - 935
12345