Compatibility of erbium oxide coating with liquid lithium-lead alloy and corrosion protection effect of iron layer

被引：20

作者：

Chikada, Takumi ^{[1
]}

Suzuki, Akihiro ^{[2
]}

Terai, Takayuki ^{[1
]}

Muroga, Takeo ^{[3
]}

Koch, Freimut ^{[4
]}

机构：

[1] Univ Tokyo, Sch Engn, Inst Engn Innovat, Tokyo, Japan

[2] Univ Tokyo, Sch Engn, Nucl Profess Sch, Tokai, Ibaraki, Japan

[3] Natl Inst Fus Sci, Dept Helical Plasma Res, Toki, Gifu, Japan

[4] Max Planck Inst Plasma Phys, Garching, Germany

来源：

FUSION ENGINEERING AND DESIGN | 2013年 / 88卷 / 6-8期

关键词：

Lithium-lead; Tritium permeation; Corrosion; Coating; Erbium oxide; TRITIUM PERMEATION BARRIERS; ARC; FILMS;

D O I：

10.1016/j.fusengdes.2013.03.075

中图分类号：

TL [原子能技术]; O571 [原子核物理学];

学科分类号：

0827 ; 082701 ;

摘要：

Li-Pb compatibility of Er2O3 and Er2O3-Fe two-layer coatings has been explored for an understanding of corrosion behaviors and effects of the protection layer. The coatings wee peeled off after static Li-Pb immersion test at 600 degrees C due to the degradation of adhesion between the coating-substrate interface. A loss of Er and then subsequent corrosion of Er2O3 were shown after immersion at 500 degrees C for 500 and 1505 h. However, the outer Fe layer played a role to decrease corrosion rate of the coatings by comparing with the results of Er2O3 single layer coatings. Deuterium permeation measurements after corrosion tests at 500 degrees C showed that the Er2O3 coatings kept permeation reduction factors of 10(2)-10(3) after 500 h immersion, but seriously degraded after 1505 h immersion. Corrosion mechanisms suggest that corrosion protection properties will be modified by an optimization of the outer Fe layer and a control of oxygen concentration in Li-Pb. (C) 2013 Elsevier B.V. All rights reserved.

引用

页码：640 / 643

页数：4

共 18 条

[1] Monoclinic B-phase erbium sesquioxide (Er2O3) thin films by filtered cathodic arc deposition [J].

Adelhelm, Christoph ;

Pickert, Thomas ;

Balden, Martin ;

Rasinski, Marcin ;

Plocinski, Tomasz ;

Ziebert, Carlos ;

Koch, Freimut ;

Maier, Hans .

SCRIPTA MATERIALIA, 2009, 61 (08) :789-792

[2] Development of tritium permeation barriers on Al base in Europe [J].

Benamati, G ;

Chabrol, C ;

Perujo, A ;

Rigal, E ;

Glasbrenner, H .

JOURNAL OF NUCLEAR MATERIALS, 1999, 271 :391-395

[3] Surface behaviour in deuterium permeation through erbium oxide coatings [J].

Chikada, T. ;

Suzuki, A. ;

Adelhelm, C. ;

Terai, T. ;

Muroga, T. .

NUCLEAR FUSION, 2011, 51 (06)

[4]

Chikada T., 2011, 15 INT C FUS REACT M

[5] MODELING OF TRITIUM PERMEATION THROUGH ERBIUM OXIDE COATINGS [J].

Chikada, Takumi ;

Suzuki, Akihiro ;

Maier, Hans ;

Terai, Takayuki ;

Muroga, Takeo .

FUSION SCIENCE AND TECHNOLOGY, 2011, 60 (01) :389-393

[6] Microstructure control and deuterium permeability of erbium oxide coating on ferritic/martensitic steels by metal-organic decomposition [J].

Chikada, Takumi ;

Suzuki, Akihiro ;

Tanaka, Teruya ;

Terai, Takayuki ;

Muroga, Takeo .

FUSION ENGINEERING AND DESIGN, 2010, 85 (7-9) :1537-1541

[7] Deuterium permeation behavior of erbium oxide coating on austenitic, ferritic, and ferritic/martensitic steels [J].

Chikada, Takumi ;

Suzuki, Akihiro ;

Yao, Zhenyu ;

Levchuk, Denis ;

Maier, Hans ;

Terai, Takayuki ;

Muroga, Takeo .

FUSION ENGINEERING AND DESIGN, 2009, 84 (2-6) :590-592

[8]

Cliikada T., 2009, FUSION SCI TECHNOL, V56, P309

[9] LITHIUM LEAD EUTECTIC AS BREEDING MATERIAL IN FUSION-REACTORS [J].

COEN, V .

JOURNAL OF NUCLEAR MATERIALS, 1985, 133 (AUG) :46-51

[10]

HOLLENBERG GW, 1995, FUSION ENG DES, V28, P190, DOI 10.1016/0920-3796(95)90039-X

← 1 2 →