Formation of rhombohedral L11 CoPt thin film on glass and MgO(111) substrate

被引：11
|
作者：
Sun, An-Cheng [1 ]
Huang, S. H. [1 ]
Huang, Chuan-Fa [1 ]
机构：
[1] Yuan Ze Univ, Dept Chem Engn & Mat Sci, Chungli 32003, Taiwan
来源：
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS | 2013年 / 345卷
关键词：
L1(1); CoPt; Thin film; Magnetic property; Magnetocrystalline anisotropy; Sputter; PERPENDICULAR MAGNETIC-ANISOTROPY;
D O I：
10.1016/j.jmmm.2013.07.003
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
L1(1) type CoPt superstructure, a rhombohedral meta-stable phase, thin films with different thickness (t) were sputtered on glass, Pt/glass, and MgO(111) substrates. Perpendicular magnetic anisotropy (PMA) is obtained as the CoPt films, which are deposited on Pt(111)/glass and MgO substrates. The coercivity (H-c) of CoPt/Pt/glass is higher than that of CoPt/MgO(111) film due to the smaller lattice misfit at CoPt/Pt interface and domain wall impedance at CoPt grain boundary. For the CoPt/Pt/glass and CoPt/MgO films, H-c usually increases with reducing the t from 50 nm to 5 nm. This result could be attributed to the roughness effect at CoPt/Pt and CoPt/MgO interfaces. Without Pt underlayer, CoPt thin film exhibits soft magnetic phase on glass substrate. In this study, higher H-c of about 141 kA/m is shown on 3 nm-thick CoPt film on Pt/glass. The improvement of perpendicular magnetic properties are obtained by replacing the MgO(111) with Pt/glass, inducing high potential of L1(1) CoPt in future applications. Crown Copyright (c) 2013 Published by Elsevier B.V. All rights reserved.
引用
收藏
页码：282 / 287
页数：6
相关论文
共 50 条
  • [31] Thin Helium Film on a Glass Substrate
    Boninsegni, Massimo
    JOURNAL OF LOW TEMPERATURE PHYSICS, 2010, 159 (3-4) : 441 - 451
  • [32] Fabrication of L11 Co-Pt-Cu perpendicular anisotropic films with enhanced coercivity on glass substrate
    Yuan, Fu-Te
    Li, Long-Jie
    Hsu, Jen-Hwa
    Hsiao, S. N.
    Lee, H. Y.
    Lu, Hsi-Chuan
    Wang, Sea-Fue
    Shen, C. Y.
    Sun, An-Cheng
    JOURNAL OF APPLIED PHYSICS, 2012, 111 (07)
  • [33] Deformation of TiAl by the formation of L11 pseudo-twin
    Xu, Dongsheng
    Wang, Hao
    Li, Yujuan
    Yang, Rui
    STRUCTURAL ALUMINIDES FOR ELEVATED TEMPERATURES: GAMMA TITANIUM AND OTHER: METALLIC ALUMINIDES, 2008, : 119 - 124
  • [34] Growth of MgO Thin Film on Silicon Substrate by MOCVD
    鲁智宽
    于淑琴
    黄柏标
    蒋民华
    王弘
    王晓临
    黄平
    RareMetals, 1993, (02) : 81 - 83
  • [35] Thermal Fluctuations in YBCO Thin Film on MgO Substrate
    Chrobak, M.
    Woch, W. M.
    Szwachta, G.
    Zalecki, R.
    Gondek, L.
    Kolodziejczyk, A.
    Kusinski, J.
    ACTA PHYSICA POLONICA A, 2014, 126 (4A) : A88 - A91
  • [36] L10 phase formation in CoPt thin films
    Ristau, RA
    Barmak, K
    Coffey, KR
    Howard, JK
    MAGNETIC ULTRATHIN FILMS, MULTILAYERS AND SURFACES - 1997, 1997, 475 : 119 - 124
  • [37] Formation of nano-sized pinholes array in thin Ni film on MgO(100) substrate
    Lin, C
    Naramoto, H
    Xu, YH
    Kitazawa, S
    Narumi, K
    Sakai, S
    THIN SOLID FILMS, 2003, 443 (1-2) : 28 - 32
  • [38] Redox of NiO thin film on YSZ (111) substrate
    Xing, Juanjuan
    Takeguchi, Masaki
    Tanaka, Miyoko
    Nakayama, Yoshiko
    SURFACE AND INTERFACE ANALYSIS, 2012, 44 (11-12) : 1483 - 1487
  • [39] Atomic and electronic structure of an unreconstructed polar MgO(111) thin film on Ag(111)
    Kiguchi, M
    Entani, S
    Saiki, K
    Goto, T
    Koma, A
    PHYSICAL REVIEW B, 2003, 68 (11):
  • [40] Triangular ferroelectric domains of highly (111)-oriented NaNbO3 thin film on a glass substrate
    Woo-Hee Kim
    Jong Yeog Son
    Electronic Materials Letters, 2014, 10 : 107 - 110
12345